1.1 This specification covers cold-applied, singlecomponent, chemically curing silicone sealants that are based on polymers of polysiloxane structures and are intended for use in sealing joints and cracks in portland cement concrete highway and airfield pavements. The specification includes both non-sag and self-leveling types of sealants.
1.1.1 This specification does not purport to cover the properties required of sealants for use in areas of portland cement concrete pavements subject to jet fuel or other fuel spillage, such as vehicle or aircraft refueling and maintenance areas, or a combination thereof.
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.
1.3 The following safety hazards caveat pertains only to the test methods portion, Section 9, of this specification: This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. Specific precautionary statements are given in Appendix X1.
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
ASTM D5893/D5893M-16(2021) Referenced Document
ASTM C1183/C1183M Standard Test Method for Extrusion Rate of Elastomeric Sealants
ASTM C639 Standard Test Method for Rheological (Flow) Properties of Elastomeric Sealants
ASTM C661 Standard Test Method for Indentation Hardness of Elastomeric-Type Sealants by Means of a Durometer
ASTM C679 Standard Test Method for Tack-Free Time of Elastomeric Sealants
ASTM C792 Standard Test Method for Effects of Heat Aging on Weight Loss, Cracking, and Chalking of Elastomeric Sealants
ASTM C793 Standard Test Method for Effects of Accelerated Weathering on Elastomeric Joint Sealants
ASTM D1985 Standard Practice for Preparing Concrete Blocks for Testing Sealants, for Joints and Cracks
ASTM D2202 Standard Test Method for Slump of Sealants*, 2023-06-01 Update
ASTM D412 Standard Test Methods for Vulcanized Rubber and Thermoplastic Elastomers8212;Tension
ASTM D5249 Standard Specification for Backer Material for Use with Cold- and Hot-Applied Joint Sealants in Portland-Cement Concrete and Asphalt Joints
ASTM D5329 Standard Test Methods for Sealants and Fillers, Hot-Applied, For Joints and Cracks in Asphaltic and Portland Cement Concrete Pavements
ASTM D5535 Standard Terminology Relating to Formed-in-Place Sealants for Joints and Cracks in Pavements
ASTM D618 Standard Practice for Conditioning Plastics for Testing*, 2021-07-15 Update
ASTM D5893/D5893M-16(2021) history
2021ASTM D5893/D5893M-16(2021) Standard Specification for Cold-Applied, Single-Component, Chemically Curing Silicone Joint Sealant for Portland Cement Concrete Pavements
2016ASTM D5893/D5893M-16 Standard Specification for Cold Applied, Single Component, Chemically Curing Silicone Joint Sealant for Portland Cement Concrete Pavements
2010ASTM D5893/D5893M-10 Standard Specification for Cold Applied, Single Component, Chemically Curing Silicone Joint Sealant for Portland Cement Concrete Pavements
2004ASTM D5893-04 Standard Specification for Cold Applied, Single Component, Chemically Curing Silicone Joint Sealant for Portland Cement Concrete Pavements
1996ASTM D5893-96 Standard Specification for Cold Applied, Single Component, Chemically Curing Silicone Joint Sealant for Portland Cement Concrete Pavements