ASTM A811-15
Standard Specification for Soft Magnetic Iron Parts Fabricated by Powder Metallurgy Techniques
- Standard No.
- ASTM A811-15
- Release Date
- 2015
- Published By
- American Society for Testing and Materials (ASTM)
- Status
- Replace By
- ASTM A811-15(2022)
- Latest
- ASTM A811-15(2022)
- Scope
1.1 This specification covers parts produced from iron powder metallurgy materials.
1.2 This specification deals with powder metallurgy parts in the sintered or annealed condition. Should the sintered parts be subjected to any secondary operation that causes mechanical strain, such as machining or sizing, they should be resintered or annealed.
1.3 The values stated in SI units are to be regarded as standard. The values given in parentheses are mathematical conversions to customary (cgs-emu and inch-pound) units, which are provided for information only, and are not considered standard.
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.
ASTM A811-15 Referenced Document
- ASTM A34/A34M Standard Practice for Sampling and Procurement Testing of Magnetic Materials
- ASTM A340 Standard Terminology of Symbols and Definitions Relating to Magnetic Testing
- ASTM A596/A596M Standard Test Method for Direct-Current Magnetic Properties of Materials Using the Ballistic Method and Ring Specimens
- ASTM A773/A773M Standard Test Method for dc Magnetic Properties of Materials Using Ring and Permeameter Procedures with dc Electronic Hysteresigraphs
- ASTM B962 Standard Test Methods for Density of Compacted or Sintered Powder Metallurgy (PM) Products Using Archimedes’ Principle
- ASTM E1019 Standard Test Methods for Determination of Carbon, Sulfur, Nitrogen, and Oxygen in Steel and in Iron, Nickel, and Cobalt Alloys*， 2024-04-20 Update
ASTM A811-15 history
- 2022 ASTM A811-15(2022) Standard Specification for Soft Magnetic Iron Parts Fabricated by Powder Metallurgy Techniques
- 2015 ASTM A811-15 Standard Specification for Soft Magnetic Iron Parts Fabricated by Powder Metallurgy Techniques
- 2003 ASTM A811-03(2008) Standard Specification for Soft Magnetic Iron Parts Fabricated by Powder Metallurgy (P/M) Techniques
- 2003 ASTM A811-03 Standard Specification for Soft Magnetic Iron Parts Fabricated by Powder Metallurgy (P/M) Techniques
- 1997 ASTM A811-97 Standard Specification for Soft Magnetic Iron Parts Fabricated by Powder Metallurgy (P/M) Techniques