ASTM A811-03(2008)
Standard Specification for Soft Magnetic Iron Parts Fabricated by Powder Metallurgy (P/M) Techniques

Standard No.

ASTM A811-03(2008)

Release Date

2003

Published By

American Society for Testing and Materials (ASTM)

Status

Be replaced

Replace By

ASTM A811-15

Latest

ASTM A811-15(2022)

Scope

1.1 This specification covers parts produced from iron powder metallurgy materials.

1.2 This specification deals with P/M parts in the sintered or annealed condition. Should the sintered parts be subjected to any secondary operation that causes mechanical strain, such as machining or sizing, they should be resintered or annealed.

1.3 The values stated in customary (cgs-emu and inch-pound) units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units which are provided for information only and are not considered standard.

ASTM A811-03(2008) history

• 2022 ASTM A811-15(2022) Standard Specification for Soft Magnetic Iron Parts Fabricated by Powder Metallurgy Techniques
• 2015 ASTM A811-15 Standard Specification for Soft Magnetic Iron Parts Fabricated by Powder Metallurgy Techniques
• 2003 ASTM A811-03(2008) Standard Specification for Soft Magnetic Iron Parts Fabricated by Powder Metallurgy (P/M) Techniques
• 2003 ASTM A811-03 Standard Specification for Soft Magnetic Iron Parts Fabricated by Powder Metallurgy (P/M) Techniques
• 1997 ASTM A811-97 Standard Specification for Soft Magnetic Iron Parts Fabricated by Powder Metallurgy (P/M) Techniques