SAE AMS6362G-2014
Steel Tubing, Seamless, 0.95Cr - 0.20Mo (0.28- 0.33C) (SAE 4130), 150 ksi (1034 MPa) Tensile Strength

Standard No.

SAE AMS6362G-2014

Release Date

2014

Published By

Society of Automotive Engineers (SAE)

Status

Be replaced 2018-11

Replace By

SAE AMS6362H-2018

Latest

SAE AMS6362H-2018

SAE AMS6362G-2014 Referenced Document

• ASTM A370-13 Standard Test Methods and Definitions for Mechanical Testing of Steel Products*， 2023-12-21 Update
• ASTM E112-13 Standard Test Methods for Determining Average Grain Size*， 2023-12-21 Update
• ASTM E1444-05 Standard Practice for Magnetic Particle Testing*， 2023-12-21 Update
• ASTM E350-12 Standard Test Methods for Chemical Analysis of Carbon Steel, Low-Alloy Steel, Silicon Electrical Steel, Ingot Iron, and Wrought Iron*， 2023-12-21 Update
• ASTM E384-11 Standard Test Method for Knoop and Vickers Hardness of Materials*， 2023-12-21 Update

SAE AMS6362G-2014 history

• 2018 SAE AMS6362H-2018 Steel Tubing@ Seamless 0.95Cr - 0.20Mo (0.28 - 0.33C) (SAE 4130) 150 ksi (1034 MPa) Tensile Strength (UNS G41300)
• 2014 SAE AMS6362G-2014 Steel Tubing, Seamless, 0.95Cr - 0.20Mo (0.28- 0.33C) (SAE 4130), 150 ksi (1034 MPa) Tensile Strength
• 2009 SAE AMS6362F-2009 Steel Tubing, Seamless 0.95Cr - 0.20Mo (0.28 - 0.33C) (SAE 4130) 150 ksi (1034 MPa) Tensile Strength
• 2005 SAE AMS6362F-2005 Steel Tubing, Seamless 0.95Cr - 0.20Mo (0.28 - 0.33C) (SAE 4130) 150 ksi (1034 MPa) Tensile Strength UNS G41300
• 1999 SAE AMS6362E-1999 Steel Tubing, Seamless 0.95Cr - 0.20Mo (0.28 - 0.33C) (SAE 4130) 150 ksi (1034 MPa) Tensile Strength
• 1994 SAE AMS6362D-1994 STEEL TUBING, SEAMLESS 0.95Cr - 0.20Mo (0.28-0.33C) (SAE 4130) 150,000 psi (1034 MPa) Tensile Strength
• 1990 SAE AMS6362D-1990 Steel Tubing@ Seamless 0.95Cr - 0.20Mo (0.28- 0.33C) (SAE 4130) 150@000 psi (1034 MPa) Tensile Strength
• 1985 SAE AMS6362C-1985 STEEL TUBING@ SEAMLESS 0.95Cr - 0.20Mo (0.28 - 0.33C) (SAE 4130) 150@000 psi (1035 MPa) Tensile Strength (UNS G41300)
• 1979 SAE AMS6362B-1979 STEEL TUBING@ SEAMLESS 0.95Cr - 0.20Mo (0.28 - 0.33C) (SAE 4130) 150@000 psi (1034 MPa) Tensile Strength (UNS G41300)
• 1972 SAE AMS6362A-1972 STEEL TUBING, SEAMLESS 0.95Cr - 0.20Mo (0.28 - 0.33C) (SAE 4130) 150,000 psi (1034 MPa) Tensile Strength
• 1942 SAE AMS6362A-1942 STEEL TUBING@ SEAMLESS 0.95Cr - 0.20Mo (0.28 - 0.33C) (SAE 4130) 150@000 psi (1034 MPa) Tensile Strength
• 1942 SAE AMS6362-1942 STEEL TUBING@ (SEAMLESS)@ ROUND Chromium Molybdenum (.27 - .33 Carbon) (150@000 T.S. -.188 Max. Wall Thickness)