SAE AMS6362-1942
STEEL TUBING@ (SEAMLESS)@ ROUND Chromium Molybdenum (.27 - .33 Carbon) (150@000 T.S. -.188 Max. Wall Thickness)
Home
SAE AMS6362-1942
Standard No.
SAE AMS6362-1942
Release Date
1942
Published By
SAE - SAE International
Status
Be replaced
2012-12
Replace By
SAE AMS6362A-1942
Latest
SAE AMS6362H-2018
SAE AMS6362-1942 history
2018
SAE AMS6362H-2018
Steel Tubing@ Seamless 0.95Cr - 0.20Mo (0.28 - 0.33C) (SAE 4130) 150 ksi (1034 MPa) Tensile Strength (UNS G41300)
2014
SAE AMS6362G-2014
Steel Tubing, Seamless, 0.95Cr - 0.20Mo (0.28- 0.33C) (SAE 4130), 150 ksi (1034 MPa) Tensile Strength
2009
SAE AMS6362F-2009
Steel Tubing, Seamless 0.95Cr - 0.20Mo (0.28 - 0.33C) (SAE 4130) 150 ksi (1034 MPa) Tensile Strength
2005
SAE AMS6362F-2005
Steel Tubing, Seamless 0.95Cr - 0.20Mo (0.28 - 0.33C) (SAE 4130) 150 ksi (1034 MPa) Tensile Strength UNS G41300
1999
SAE AMS6362E-1999
Steel Tubing, Seamless 0.95Cr - 0.20Mo (0.28 - 0.33C) (SAE 4130) 150 ksi (1034 MPa) Tensile Strength
1994
SAE AMS6362D-1994
STEEL TUBING, SEAMLESS 0.95Cr - 0.20Mo (0.28-0.33C) (SAE 4130) 150,000 psi (1034 MPa) Tensile Strength
1990
SAE AMS6362D-1990
Steel Tubing@ Seamless 0.95Cr - 0.20Mo (0.28- 0.33C) (SAE 4130) 150@000 psi (1034 MPa) Tensile Strength
1985
SAE AMS6362C-1985
STEEL TUBING@ SEAMLESS 0.95Cr - 0.20Mo (0.28 - 0.33C) (SAE 4130) 150@000 psi (1035 MPa) Tensile Strength (UNS G41300)
1979
SAE AMS6362B-1979
STEEL TUBING@ SEAMLESS 0.95Cr - 0.20Mo (0.28 - 0.33C) (SAE 4130) 150@000 psi (1034 MPa) Tensile Strength (UNS G41300)
1972
SAE AMS6362A-1972
STEEL TUBING, SEAMLESS 0.95Cr - 0.20Mo (0.28 - 0.33C) (SAE 4130) 150,000 psi (1034 MPa) Tensile Strength
1942
SAE AMS6362A-1942
STEEL TUBING@ SEAMLESS 0.95Cr - 0.20Mo (0.28 - 0.33C) (SAE 4130) 150@000 psi (1034 MPa) Tensile Strength
1942
SAE AMS6362-1942
STEEL TUBING@ (SEAMLESS)@ ROUND Chromium Molybdenum (.27 - .33 Carbon) (150@000 T.S. -.188 Max. Wall Thickness)
Copyright ©2023 All Rights Reserved