ASTM D885/D885M-10A(2014)e1
Standard Test Methods for Tire Cords, Tire Cord Fabrics, and Industrial Filament Yarns Made from Manufactured Organic-Base Fibers

Standard No.

ASTM D885/D885M-10A(2014)e1

Release Date

2010

Published By

American Society for Testing and Materials (ASTM)

Status

Be replaced

Replace By

ASTM D885/D885M-10a

Latest

ASTM D885/D885M-10a(2014)

Scope

5.1 The procedures in these test methods should be used with caution for acceptance of commercial shipments owing to the absence of factual information on the between-laboratory precision of many of the test procedures included in these test methods. It is recommended that any program of acceptance testing be preceded by an interlaboratory check in the laboratory of the purchaser and the laboratory of the supplier on replicate specimens of the materials to be tested for each property (or properties) to be evaluated.

5.1.1 If there are differences of practical significance between reported test results for two laboratories (or more), comparative tests should be performed to determine if there is a statistical bias between them, using competent statistical assistance. As a minimum, test samples should be used that are as homogeneous as possible, that are drawn from the material from which the disparate test results were obtained, and that are randomly assigned in equal numbers to each laboratory for testing. Other materials with established test values may be used for this purpose. The test results from the two laboratories should be compared using a statistical test for unpaired data, at a probability level chosen prior to the testing series. If a bias is found, either its cause must be found and corrected, or future test results must be adjusted in consideration of the known bias.

5.2 The significance and use of particular properties are discussed in the appropriate sections of specific test methods.

1.1 These test methods cover the testing of industrial filament yarns made wholly of manufactured organic-base fibers, cords twisted from such yarns, fabrics woven from such cords, and products that are made specifically for use in the manufacture of pneumatic tires. They may be applied to similar yarns and cords used for reinforcing other rubber goods and for other industrial applications. The test methods apply to nylon, polyester, and rayon yarns and tire cords twisted from such yarns and to fabrics made from such cords. The yarn or cord may be wound on cones, tubes, bobbins, spools, or beams; may be woven into fabric; or may be in some other form. The methods include testing procedure only and include no specifications or tolerances.

1.2 No procedure is included for the determination of fatigue resistance of cord, but several commonly used procedures for the measurement of fatigue resistance of cords in rubber were published in the appendix of these test methods in the 1967 Annual Book of ASTM Standards, Part 24, and in earlier issues of Test Methods D885.

1.3 The sections on “Growth of Conditioned Yarns and Cords,” “Properties of Yarns and Cords at Elevated Temperature,” and “Properties of Wet Yarns and Cords” have been moved to Appendix X1 – Appendix X3 as non-mandatory informational items because of their very limited use by the industry and because precision and bias statements are not included.

1.4 This standard includes the following sections:

ASTM D885/D885M-10A(2014)e1 Referenced Document

• ASTM D123 Standard Terminology Relating to Textiles
• ASTM D1423 Standard Test Method for Twist in Yarns by Direct-Counting
• ASTM D1776 Standard Practice for Conditioning and Testing Textiles
• ASTM D1777 Standard Test Method for Thickness of Textile Materials
• ASTM D1907 Standard Test Method for Linear Density of Yarn (Yarn Number) by the Skein Method
• ASTM D1909 Standard Table of Commercial Moisture Regains for Textile Fibers
• ASTM D2257 Standard Test Method for Extractable Matter in Textiles
• ASTM D2258 Standard Practice for Sampling Yarn for Testing
• ASTM D2462 Standard Test Method for Moisture in Wool by Distillation With Toluene
• ASTM D2494 Standard Test Method for Commercial Mass of a Shipment of Yarn or Man-Made Staple Fiber or Tow
• ASTM D2654 Standard Test Methods for Moisture in Textiles
• ASTM D276 Standard Test Methods for Identification of Fibers in Textiles*， 2024-04-20 Update
• ASTM D3774 Standard Test Method for Width of Textile Fabric
• ASTM D3775 Standard Test Method for Fabric Count of Woven Fabric
• ASTM D3776 Standard Test Methods for Mass Per Unit Area (Weight) of Fabric
• ASTM D4393 Standard Test Method for Strap Peel Adhesion of Reinforcing Cords or Fabrics to Rubber Compounds
• ASTM D4776 Standard Test Method for Adhesion of Tire Cords and Other Reinforcing Cords to Rubber Compounds by H-Test Procedure
• ASTM D4848 Standard Terminology Related to Force, Deformation and Related Properties of Textiles
• ASTM D6477 Standard Terminology Relating to Tire Cord and Fabrics
• ASTM D76 Standard Specification for Tensile Testing Machines for Textiles

ASTM D885/D885M-10A(2014)e1 history

• 2010 ASTM D885/D885M-10a(2014) Standard Test Methods for Tire Cords, Tire Cord Fabrics, and Industrial Filament Yarns Made from Manufactured Organic-Base Fibers
• 2010 ASTM D885/D885M-10a Standard Test Methods for Tire Cords, Tire Cord Fabrics, and Industrial Filament Yarns Made from Manufactured Organic-Base Fibers
• 2010 ASTM D885/D885M-10A(2014)e1 Standard Test Methods for Tire Cords, Tire Cord Fabrics, and Industrial Filament Yarns Made from Manufactured Organic-Base Fibers
• 2010 ASTM D885/D885M-10 Standard Test Methods for Tire Cords, Tire Cord Fabrics, and Industrial Filament Yarns Made from Manufactured Organic-Base Fibers
• 2007 ASTM D885-07e1 Standard Test Methods for Tire Cords, Tire Cord Fabrics, and Industrial Filament Yarns Made from Manufactured Organic-Base Fibers
• 2007 ASTM D885-07 Standard Test Methods for Tire Cords, Tire Cord Fabrics, and Industrial Filament Yarns Made from Manufactured Organic-Base Fibers
• 2006 ASTM D885-06 Standard Test Methods for Tire Cords, Tire Cord Fabrics, and Industrial Filament Yarns Made from Manufactured Organic-Base Fibers
• 2004 ASTM D885-04 Standard Test Methods for Tire Cords, Tire Cord Fabrics, and Industrial Filament Yarns Made from Man-Made Organic-Base Fibers
• 2003 ASTM D885-03 Standard Test Methods for Tire Cords, Tire Cord Fabrics, and Industrial Filament Yarns Made from Man-Made Organic-Base Fibers
• 2002 ASTM D885-02a Standard Test Methods for Tire Cords, Tire Cord Fabrics, and Industrial Filament Yarns Made from Man-Made Organic-Base Fibers
• 2002 ASTM D885-02 Standard Test Methods for Tire Cords, Tire Cord Fabrics, and Industrial Filament Yarns Made from Man-Made Organic-Base Fibers
• 2001 ASTM D885-01 Standard Test Methods for Tire Cords, Tire Cord Fabrics, and Industrial Filament Yarns Made from Man-Made Organic-Base Fibers
• 2001 ASTM D885-98 Standard Test Methods for Tire Cords, Tire Cord Fabrics, and Industrial Filament Yarns Made from Man-Made Organic-Base Fibers