1.1 This test method covers the determination of the shear properties of high-modulus fiber-reinforced composite materials by clamping the ends of a V-notched specimen between two pairs of loading rails. When loaded in tension, the rails introduce shear forces into the specimen through the specimen faces. In comparison, the specimen of Test Method D5379/D5379M is loaded through its top and bottom edges. Face loading allows higher shear forces to be applied to the specimen, if required. Additionally, the present test method utilizes a specimen with a larger gage section than the V-notched specimen of Test Method D5379/D5379M. In both test methods, the use of a V-notched specimen increases the gage section shear stresses in relation to the shear stresses in the vicinity of the grips, thus localizing the failure within the gage section while causing the shear stress distribution to be more uniform than in a specimen without notches. In comparison, Test Method D4255/D4255M utilizes an unnotched specimen clamped between two pairs of loading rails that are loaded in tension. Also in contrast to Test Method
ASTM D7078/D7078M-12 Referenced Document
ASTM D2584 Standard Test Method for Ignition Loss of Cured Reinforced Resins
ASTM D2734 Standard Test Methods for Void Content of Reinforced Plastics
ASTM D3171 Standard Test Methods for Constituent Content of Composite Materials
ASTM D3878 Standard Terminology Composite Materials
ASTM D4255/D4255M Standard Test Method for In-Plane Shear Properties of Polymer Matrix Composite Materials by the Rail Shear Method
ASTM D5229/D5229M Standard Test Method for Moisture Absorption Properties and Equilibrium Conditioning of Polymer Matrix Composite Materials
ASTM D5379/D5379M Standard Test Method for Shear Properties of Composite Materials by the V-Notched Beam Method
ASTM D6856 Standard Guide for Testing Fabric-Reinforced "Textile" Composite Materials
ASTM D792 Standard Test Methods for Density and Specific Gravity (Relative Density) of Plastics by Displacement
ASTM D883 Standard Terminology Relating to Plastics
ASTM E111 Standard Test Method for Young''s Modulus, Tangent Modulus, and Chord Modulus
ASTM E122 Standard Practice for Calculating Sample Size to Estimate, With a Specified Tolerable Error, the Average for Characteristic of a Lot or Process
ASTM E1237 Standard Guide for Installing Bonded Resistance Strain Gages
ASTM E1309 Standard Guide for Identification of Fiber-Reinforced Polymer-Matrix Composite Materials in Databases
ASTM E1434 Standard Guide for Recording Mechanical Test Data of Fiber-Reinforced Composite Materials in Databases
ASTM E177 Standard Practice for Use of the Terms Precision and Bias in ASTM Test Methods
ASTM E251 Standard Test Methods for Performance Characteristics of Metallic Bonded Resistance Strain Gages
ASTM E4 Standard Practices for Force Verification of Testing Machines
ASTM E456 Standard Terminology for Relating to Quality and Statistics
ASTM E6 Standard Terminology Relating to Methods of Mechanical Testing
ASTM D7078/D7078M-12 history
2020ASTM D7078/D7078M-20e1 Standard Test Method for Shear Properties of Composite Materials by V-Notched Rail Shear Method
2020ASTM D7078/D7078M-20 Standard Test Method for Shear Properties of Composite Materials by V-Notched Rail Shear Method
2019ASTM D7078/D7078M-19 Standard Test Method for Shear Properties of Composite Materials by V-Notched Rail Shear Method
2012ASTM D7078/D7078M-12 Standard Test Method for Shear Properties of Composite Materials by V-Notched Rail Shear Method
2005ASTM D7078/D7078M-05 Standard Test Method for Shear Properties of Composite Materials by V-Notched Rail Shear Method