SAE AMS2451/9B-2012
Plating, Brush, Zinc-Nickel Low Hydrogen Embrittlement

Standard No.
SAE AMS2451/9B-2012
Release Date
2012
Published By
Society of Automotive Engineers (SAE)
Latest
SAE AMS2451/9B-2012
Scope
This specification covers the engineering requirements and processes for brush plating of zinc-nickel by electrodeposition. This process has been used typically to improve corrosion resistance of steel parts operating under 500 °F (260 °C) asplated or under 250 °F (121 °C) when chromate treated, to repair zinc-nickel deposits and to repair damaged or worn parts, but usage is not limited to such applications.

SAE AMS2451/9B-2012 Referenced Document

SAE AMS2451/9B-2012 history

SAE AMS2451/9B-2012 -All Parts

SAE AMS2451-1998 Plating@ Brush General Requirements SAE AMS2451/1-1998 Plating, Brush, Nickel General Purpose SAE AMS2451/10-2002 Plating, Brush, Tin-Zinc Low Hydrogen Embrittlement SAE AMS2451/10A-2011 Plating, Brush, Tin-Zinc Low Hydrogen Embrittlement SAE AMS2451/10B-2018 Plating@ Brush@ Tin-Zinc Low Hydrogen Embrittlement SAE AMS2451/10C-2023 Plating, Brush, Tin-Zinc Low Hydrogen Embrittlement SAE AMS2451/11-2001 Plating, Brush, Cobalt SAE AMS2451/11A-2011 Plating, Brush, Cobalt SAE AMS2451/11B-2022 Plating, Brush, Cobalt SAE AMS2451/12-2011 Plating, Brush, Tin SAE AMS2451/12A-2022 Plating, Brush, Tin SAE AMS2451/13-2011 Plating, Brush, Silver SAE AMS2451/13A-2022 Plating, Brush, Silver SAE AMS2451/14-2022 Plating, Brush, Nickel-Tungsten Low Hydrogen Embrittlement SAE AMS2451/1A-2011 Plating, Brush, Nickel General Purpose SAE AMS2451/1B-2022 Plating, Brush, Nickel General Purpose SAE AMS2451/2-1998 Plating, Brush, Nickel Low Stress, Hard Deposit SAE AMS2451/2A-2011 Plating, Brush, Nickel Low Stress, Hard Deposit SAE AMS2451/2B-2022 Plating, Brush, Nickel Low Stress, Hard Deposit SAE AMS2451/3-1998 Plating, Brush, Nickel Low Stress, Low-Hardness Deposit SAE AMS2451/3A-2011 Plating, Brush, Nickel Low Stress, Low-Hardness Deposit SAE AMS2451/3B-2016 Plating@ Brush@ Nickel Low Stress@ Low-Hardness Deposit SAE AMS2451/3C-2017 Plating@ Brush@ Nickel Low Stress@ Low-Hardness Deposit SAE AMS2451/3D-2022 Plating, Brush, Nickel Low-Stress, Low-Hardness Deposit SAE AMS2451/4-1998 Plating@ Brush@ Cadmium Corrosion Protective@ Low Hydrogen Embrittlement SAE AMS2451/4A-2002 Plating, Brush, Cadmium Corrosion Protective, Low Hydrogen Embrittlement SAE AMS2451/4B-2011 Plating, Brush, Cadmium Corrosion Protective, Low Hydrogen Embrittlement SAE AMS2451/4C-2017 Plating@ Brush@ Cadmium Corrosion Protective@ Low Hydrogen Embrittlement SAE AMS2451/4D-2017 Plating@ Brush@ Cadmium Corrosion Protective@ Low Hydrogen Embrittlement SAE AMS2451/4E-2022 Plating, Brush, Cadmium Corrosion Protective, Low Hydrogen Embrittlement SAE AMS2451/5-1998 Plating, Brush, Chromium Hard Deposit, Trivalent SAE AMS2451/5A-2011 Plating, Brush, Chromium Hard Deposit, Trivalent SAE AMS2451/5B-2017 Plating@ Brush@ Chromium Hard Deposit@ Trivalent SAE AMS2451/5C-2021 Plating, Brush, Chromium Hard Deposit, Trivalent SAE AMS2451/6-1998 Plating, Brush, Copper General Purpose SAE AMS2451/6A-2011 Plating, Brush, Copper General Purpose


Copyright ©2024 All Rights Reserved