SAE AMS4786H-2009
Gold-Palladium-Nickel Alloy, Brazing Filler Metal, High Temperature, 70Au 8.0Pd 22Ni, 1845 to 1915°F (1007 to 1046°C) Solidus-Liquidus Range

Standard No.

SAE AMS4786H-2009

Release Date

2009

Published By

Society of Automotive Engineers (SAE)

Status

Be replaced

Replace By

SAE AMS4786J-2015

Latest

SAE AMS4786K-2021

Scope

SAE AMS 4786H restores this document to active status. This specification covers a gold-palladium-nickel alloy in the form of wire, rod, sheet, strip, foil, pig, powder, shot, and chips and a viscous mixture (paste) of powder in a suitable binder. This filler metal has been used typically for joining corrosion and heat resistant steels and alloys where corrosion and oxidation resistant joints with good strength at elevated temperatures are required but usage is not limited to such applications.

SAE AMS4786H-2009 Referenced Document

• ASTM B214-07 Standard Test Method for Sieve Analysis of Metal Powders*， 2024-04-19 Update
• SAE AMS2222 TOLERANCES Copper and Copper Alloy Plate@ Sheet and Strip
• SAE AMS2222J-2006 Tolerances Copper and Copper Alloy Sheet, Strip, and Plate
• SAE AMS2224 Tolerances Copper and Copper Alloy Wire
• SAE AMS2224G-2006 Tolerances Copper and Copper Alloy Wire

SAE AMS4786H-2009 history

• 2021 SAE AMS4786K-2021 Gold-Palladium-Nickel Alloy, Brazing Filler Metal, High Temperature 70Au - 8.0Pd - 22Ni 1845 to 1915 °F (1007 to 1046 °C) Solidus-Liquidus Range (UNS P00700)
• 2015 SAE AMS4786J-2015 Gold-Palladium-Nickel Alloy@ Brazing Filler Metal@ High Temperature 70Au �C 8.0Pd �C 22Ni 1845 to 1915 ��(1007 to 1046 �� Solidus-Liquidus Range (UNS P00700)
• 2009 SAE AMS4786H-2009 Gold-Palladium-Nickel Alloy, Brazing Filler Metal, High Temperature, 70Au 8.0Pd 22Ni, 1845 to 1915°F (1007 to 1046°C) Solidus-Liquidus Range
• 2007 SAE AMS4786G-2007 Gold-Palladium-Nickel Alloy@ Brazing Filler Metal@ High Temperature 70Au - 8.0Pd - 22Ni 1845 to 1915 °F (1007 to 1046 °C) Solidus-Liquidus Range (UNS P00700)
• 2002 SAE AMS4786F-2002 Gold-Palladium-Nickel Alloy, Brazing Filler Metal, High Temperature 70Au - 8.0Pd - 22Ni 1845 to 1915 °F (1007 to 1046 °C) Solidus-Liquidus Range
• 2001 SAE AMS4786F-2001 Gold-Palladium-Nickel Alloy, Brazing Filler Metal, High Temperature 70Au - 8.0Pd - 22Ni 1845 to 1915 °F (1007 to 1046 °C) Solidus-Liquidus Range UNS P00700
• 1999 SAE AMS4786E-1999 Gold-Palladium-Nickel Alloy@ Brazing Filler Metal@ High Temperature 70Au - 8.0Pd - 22Ni 1845 to 1915 Degrees F (1007 to 1046 Degrees C) Solidus-Liquidus Range (UNS P00700)
• 1992 SAE AMS4786D-1992 Gold-Palladium-Nickel Alloy Brazing Filler Metal@ High Temperature 70Au - 8.0Pd - 22Ni 1845 to 1915 Degrees F (1007 to 1046 Degrees C) Solidus-Liquidus Range
• 1990 SAE AMS4786C-1990 BRAZING FILLER METAL@ HIGH TEMPERATURE 70Au - 8.0Pd - 22Ni 1845° - 1915° F (1007° - 1046° C) Solidus-Liquidus Range (UNS P00700)
• 1984 SAE AMS4786B-1984 BRAZING FILLER METAL@ HIGH TEMPERATURE 70Au - 8.0Pd - 22Ni 1845° - 1915°F (1005° - 1045°C) Solidus-Liquidus Range (UNS P00700)
• 1978 SAE AMS4786A-1978 BRAZING FILLER METAL@ HIGH TEMPERATURE 70Au - 8.0Pd - 22Ni 1845° - 1915° F (1005° - 1045° C) Solidus-Liquidus Range (UNS P00700)
• 1968 SAE AMS4786-1968 BRAZING FILLER METAL@ HIGH TEMPERATURE 70Au - 8Pd - 22Ni