SAE AMS4786B-1984
BRAZING FILLER METAL@ HIGH TEMPERATURE 70Au - 8.0Pd - 22Ni 1845° - 1915°F (1005° - 1045°C) Solidus-Liquidus Range (UNS P00700)

Standard No.

SAE AMS4786B-1984

Release Date

1984

Published By

SAE - SAE International

Status

Be replaced 2012-12

Replace By

SAE AMS4786C-1990

Latest

SAE AMS4786K-2021

Scope

Form: this specification covers a gold-palladium-nickel alloy in the form of wire@ rod@ sheet@ strip@ foil@ pig@ powder@ shot@ and chips and a viscous mixture (paste) of powder in a suitable binder. Application: Primarily for joining corrosion and heat resistant steels and alloy where corrosion ad oxidation resistant joint with good strength at elevated temperatures are required.

SAE AMS4786B-1984 history

• 2021 SAE AMS4786K-2021 Gold-Palladium-Nickel Alloy, Brazing Filler Metal, High Temperature 70Au - 8.0Pd - 22Ni 1845 to 1915 °F (1007 to 1046 °C) Solidus-Liquidus Range (UNS P00700)
• 2015 SAE AMS4786J-2015 Gold-Palladium-Nickel Alloy@ Brazing Filler Metal@ High Temperature 70Au �C 8.0Pd �C 22Ni 1845 to 1915 ��(1007 to 1046 �� Solidus-Liquidus Range (UNS P00700)
• 2009 SAE AMS4786H-2009 Gold-Palladium-Nickel Alloy, Brazing Filler Metal, High Temperature, 70Au 8.0Pd 22Ni, 1845 to 1915°F (1007 to 1046°C) Solidus-Liquidus Range
• 2007 SAE AMS4786G-2007 Gold-Palladium-Nickel Alloy@ Brazing Filler Metal@ High Temperature 70Au - 8.0Pd - 22Ni 1845 to 1915 °F (1007 to 1046 °C) Solidus-Liquidus Range (UNS P00700)
• 2002 SAE AMS4786F-2002 Gold-Palladium-Nickel Alloy, Brazing Filler Metal, High Temperature 70Au - 8.0Pd - 22Ni 1845 to 1915 °F (1007 to 1046 °C) Solidus-Liquidus Range
• 2001 SAE AMS4786F-2001 Gold-Palladium-Nickel Alloy, Brazing Filler Metal, High Temperature 70Au - 8.0Pd - 22Ni 1845 to 1915 °F (1007 to 1046 °C) Solidus-Liquidus Range UNS P00700
• 1999 SAE AMS4786E-1999 Gold-Palladium-Nickel Alloy@ Brazing Filler Metal@ High Temperature 70Au - 8.0Pd - 22Ni 1845 to 1915 Degrees F (1007 to 1046 Degrees C) Solidus-Liquidus Range (UNS P00700)
• 1992 SAE AMS4786D-1992 Gold-Palladium-Nickel Alloy Brazing Filler Metal@ High Temperature 70Au - 8.0Pd - 22Ni 1845 to 1915 Degrees F (1007 to 1046 Degrees C) Solidus-Liquidus Range
• 1990 SAE AMS4786C-1990 BRAZING FILLER METAL@ HIGH TEMPERATURE 70Au - 8.0Pd - 22Ni 1845° - 1915° F (1007° - 1046° C) Solidus-Liquidus Range (UNS P00700)
• 1984 SAE AMS4786B-1984 BRAZING FILLER METAL@ HIGH TEMPERATURE 70Au - 8.0Pd - 22Ni 1845° - 1915°F (1005° - 1045°C) Solidus-Liquidus Range (UNS P00700)
• 1978 SAE AMS4786A-1978 BRAZING FILLER METAL@ HIGH TEMPERATURE 70Au - 8.0Pd - 22Ni 1845° - 1915° F (1005° - 1045° C) Solidus-Liquidus Range (UNS P00700)
• 1968 SAE AMS4786-1968 BRAZING FILLER METAL@ HIGH TEMPERATURE 70Au - 8Pd - 22Ni