ASTM C1212-98(2004)
Standard Practice for Fabricating Ceramic Reference Specimens Containing Seeded Voids

Standard No.

ASTM C1212-98(2004)

Release Date

1998

Published By

American Society for Testing and Materials (ASTM)

Status

Be replaced

Replace By

ASTM C1212-98(2010)

Latest

ASTM C1212-98(2015)

Scope

This practice describes a method of fabricating known discontinuities in a ceramic specimen. Such specimens are needed and used in nondestructive examination to demonstrate sensitivity and resolution and to assist in establishing proper examination parameters.

1.1 This practice describes procedures for fabricating both green and sintered test bars of silicon carbide and silicon nitride containing both internal and surface voids at prescribed locations.

1.2 The values stated in SI units are to be regarded as the standard.

1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

ASTM C1212-98(2004) Referenced Document

• ASTM B311 Test Method for Density Determination for Powder Metallurgy (P/M) Materials Containing Less Than Two Percent Porosity
• ASTM C373 Standard Test Method for Water Absorption, Bulk Density, Apparent Porosity, and Apparent Specific Gravity of Fired Whiteware Products

ASTM C1212-98(2004) history

• 1998 ASTM C1212-98(2015) Standard Practice for Fabricating Ceramic Reference Specimens Containing Seeded Voids
• 1998 ASTM C1212-98(2010) Standard Practice for Fabricating Ceramic Reference Specimens Containing Seeded Voids
• 1998 ASTM C1212-98(2004) Standard Practice for Fabricating Ceramic Reference Specimens Containing Seeded Voids
• 1998 ASTM C1212-98 Standard Practice for Fabricating Ceramic Reference Specimens Containing Seeded Voids