ASTM B311-93(2002)e1
Test Method for Density Determination for Powder Metallurgy (P/M) Materials Containing Less Than Two Percent Porosity

Standard No.
ASTM B311-93(2002)e1
Release Date
1993
Published By
American Society for Testing and Materials (ASTM)
Status
Replace By
ASTM B311-08
Latest
ASTM B311-22
Scope

For P/M materials containing less than two percent porosity, a density measurement may be used to determine if the part has been densified, either overall or in a critical region, to the degree required for the intended application. Density alone cannot be used for evaluating the degree of densification because chemical composition and heat treatment affect the pore-free density.

For cemented carbides, a density measurement is normally used to determine if there is any significant deviation in composition of the carbide grade. For straight tungsten carbide-cobalt grades, the relationship is straightforward. For complex carbide grades (for example, grades containing tantalum carbide or titanium carbide, or both, in addition to tungsten carbide-cobalt), the situation is more complicated. If the measured density is beyond the specified limits, the composition is outside of the specified limits. A measured density within the specified limits does not ensure correct composition; compensation between two or more constituents could result in the expected density with the wrong composition. Density alone cannot be used for evaluating a cemented carbide grade.

1.1 This test method covers the determination of density for powder metallurgy (P/M) materials containing less than two percent porosity and for cemented carbides. This test method is based on the water displacement method.

Note 18212;A test specimen that gains mass when immersed in water indicates the specimen contains surface-connected porosity. Unsealed surface porosity will absorb water and cause density values higher than the true value. This test method is not applicable if this problem occurs.

1.2 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.

1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

ASTM B311-93(2002)e1 history

  • 2022 ASTM B311-22 Standard Test Method for Density of Powder Metallurgy (PM) Materials Containing Less Than Two Percent Porosity
  • 2017 ASTM B311-17(2017) Standard Test Method for Density of Powder Metallurgy (PM) Materials Containing Less Than Two Percent Porosity
  • 2013 ASTM B311-13 Standard Test Method for Density of Powder Metallurgy (PM) Materials Containing Less Than Two Percent Porosity
  • 2008 ASTM B311-08 Standard Test Method for Density of Powder Metallurgy (PM) Materials Containing Less Than Two Percent Porosity
  • 1993 ASTM B311-93(2002)e1 Test Method for Density Determination for Powder Metallurgy (P/M) Materials Containing Less Than Two Percent Porosity
  • 1997 ASTM B311-93(1997) Test Method for Density Determination for Powder Metallurgy (P/M) Materials Containing Less Than Two Percent Porosity



Copyright ©2024 All Rights Reserved