SAE AMS6386C-2000
Steel Sheet and Plate Low Alloy, Heat Treated 90,000 psi (621 MPa) and 100,000 psi (690 MPa) Yield Strength
Home
SAE AMS6386C-2000
Standard No.
SAE AMS6386C-2000
Release Date
2000
Published By
Society of Automotive Engineers (SAE)
Status
Be replaced
Replace By
SAE AMS6386C-2011
Latest
SAE AMS6386D-2016
Scope
Primarily for large structural parts requiring a good combination of strength, formability, and weldability without subsequent heat treatment.
SAE AMS6386C-2000 Referenced Document
SAE AMS2252
TOLERANCES Alloy Steel Sheet and Strip
SAE AMS2350BA-1989
STANDARDS AND TEST METHODS
SAE AMS6386C-2000 history
2016
SAE AMS6386D-2016
Steel Sheet and Plate Low Alloy@ Heat Treated 90@000 psi (621 MPa) and 100@000 psi (690 MPa) Yield Strength
2011
SAE AMS6386C-2011
Steel Sheet and Plate Low Alloy, Heat Treated 90,000 psi (621 MPa) and 100,000 psi (690 MPa) Yield Strength
2000
SAE AMS6386C-2000
Steel Sheet and Plate Low Alloy, Heat Treated 90,000 psi (621 MPa) and 100,000 psi (690 MPa) Yield Strength
1994
SAE AMS6386B-1994
STEEL SHEET AND PLATE Low Alloy, Heat Treated 90,000 psi (621 MPa) and 100,000 psi (690 MPa) Yield Strength
1974
SAE AMS6386B-1974
Steel Sheet and Plate Low Alloy@ Heat Treated 90@000 psi (621 MPa) and 100@000 psi (690 MPa) Yield Strength
1969
SAE AMS6386A-1969
STEEL SHEET AND PLATE Low Alloy@ Heat Treated 90@000 and 100@000 psi Yield Strength
1961
SAE AMS6386-1961
STEEL SHEET AND PLATE Low Alloy@ Heat Treated 100@000 psi Yield Strength
Copyright ©2024 All Rights Reserved