SAE AMS6386D-2016 PDF

Scope: Form: This specification covers high-strength@ low-alloy steels in the form of sheet and plate up to 4.000 in. (101.60 mm) in nominal thickness. Application: Primarily for large structural parts requiring a good combination of strength@ formability@ and weldability without subsequent heat treatment.

SAE AMS6386D-2016 history

2016 SAE AMS6386D-2016 Steel Sheet and Plate Low Alloy@ Heat Treated 90@000 psi (621 MPa) and 100@000 psi (690 MPa) Yield Strength
2011 SAE AMS6386C-2011 Steel Sheet and Plate Low Alloy, Heat Treated 90,000 psi (621 MPa) and 100,000 psi (690 MPa) Yield Strength
2000 SAE AMS6386C-2000 Steel Sheet and Plate Low Alloy, Heat Treated 90,000 psi (621 MPa) and 100,000 psi (690 MPa) Yield Strength
1994 SAE AMS6386B-1994 STEEL SHEET AND PLATE Low Alloy, Heat Treated 90,000 psi (621 MPa) and 100,000 psi (690 MPa) Yield Strength
1974 SAE AMS6386B-1974 Steel Sheet and Plate Low Alloy@ Heat Treated 90@000 psi (621 MPa) and 100@000 psi (690 MPa) Yield Strength
1969 SAE AMS6386A-1969 STEEL SHEET AND PLATE Low Alloy@ Heat Treated 90@000 and 100@000 psi Yield Strength
1961 SAE AMS6386-1961 STEEL SHEET AND PLATE Low Alloy@ Heat Treated 100@000 psi Yield Strength