SAE AMS4785F-2001
Gold-Palladium-Nickel Alloy Brazing Filler Metal, High Temperature, 30Au 34Pd 36Ni, 2075 to 2130°F (1135 to 1166°C) Solidus-Liquidus Range

Standard No.

SAE AMS4785F-2001

Release Date

2001

Published By

Society of Automotive Engineers (SAE)

Status

Be replaced

Replace By

SAE AMS4785F-2002

Latest

SAE AMS4785K-2021

Scope

This specification covers a gold-palladium-nickel alloy in the form of wire, rod, sheet, strip, foil, pig,powder, shot, chips, preforms, and a viscous mixture (paste) of the powder in a suitable binder.This filler metal has been used typically for joining corrosion and heat-resistant steels and alloyswhere corrosion and oxidation-resistant joints with good strength at elevated temperatures arerequired, but usage is not limited to such applications.

SAE AMS4785F-2001 history

• 2021 SAE AMS4785K-2021 Gold-Palladium-Nickel Alloy, Brazing Filler Metal, High Temperature 30Au - 34Pd - 36Ni 2075 to 2130 °F (1135 to 1166 °C) Solidus-Liquidus Range (UNS P00300)
• 2015 SAE AMS4785J-2015 Gold-Palladium-Nickel Alloy@ Brazing Filler Metal@ High Temperature 30Au – 34Pd – 36Ni 2075 to 2130 °F (1135 to 1166 °C) Solidus-Liquidus Range (UNS P00300)
• 2009 SAE AMS4785H-2009 Gold-Palladium-Nickel Alloy Brazing Filler Metal, High Temperature, 30Au 34Pd 36Ni, 2075 to 2130°F (1135 to 1166°C) Solidus-Liquidus Range
• 2007 SAE AMS4785G-2007 Gold-Palladium-Nickel Alloy@ Brazing Filler Metal@ High Temperature 30Au - 34Pd - 36Ni 2075 to 2130 °F (1135 to 1166 °C) Solidus-Liquidus Range (UNS P00300)
• 2002 SAE AMS4785F-2002 Gold-Palladium-Nickel Alloy, Brazing Filler Metal, High Temperature 30Au - 34Pd - 36Ni 2075 to 2130 °F (1135 to 1166 °C) Solidus-Liquidus Range
• 2001 SAE AMS4785F-2001 Gold-Palladium-Nickel Alloy Brazing Filler Metal, High Temperature, 30Au 34Pd 36Ni, 2075 to 2130°F (1135 to 1166°C) Solidus-Liquidus Range
• 1999 SAE AMS4785E-1999 Gold-Palladium-Nickel Alloy@ Brazing Filler Metal@ High Temperature 30Au - 34Pd - 36Ni 2075 to 2130 °F (1135 to 1166 °C) Solidus-Liquidus Range (UNS P00300)
• 1992 SAE AMS4785D-1992 Gold-Palladium-Nickel Alloy Brazing Filler Metal@ High Temperature 30Au - 34Pd - 36Ni 2075 to 2130 Degrees F (1135 to 1166 Degrees C) Solidus-Liquidus Range
• 1990 SAE AMS4785C-1990 BRAZING FILLER METAL@ HIGH TEMPERATURE 30Au - 34Pd - 36Ni 2075° - 2130°F (1135° - 1166°C) Solidus-Liquidus Range (UNS P00300)
• 1984 SAE AMS4785B-1984 BRAZING FILLER METAL@ HIGH TEMPERATURE 30Au - 34Pd - 36Ni 2075° - 2130°F (1135° - 1165°C) Solidus-Liquidus Range (UNS P00300)
• 1978 SAE AMS4785A-1978 BRAZING FILLER METAL@ HIGH TEMPERATURE 30Au - 34Pd - 36Ni 2075° - 2130°F (1135° - 1166°C) Solidus-Liquidus Range
• 1968 SAE AMS4785-1968 BRAZING FILLER METAL@ HIGH TEMPERATURE 30Au - 34Pd - 36Ni