SAE AMS4785-1968
BRAZING FILLER METAL@ HIGH TEMPERATURE 30Au - 34Pd - 36Ni

Standard No.

SAE AMS4785-1968

Release Date

1968

Published By

SAE - SAE International

Status

Be replaced 2012-12

Replace By

SAE AMS4785A-1978

Latest

SAE AMS4785K-2021

Scope

APPLICATION: Primarily for joining corrosion and heat resistant alloys where corrosion and oxidation resistant joints with good strength at high temperatures are required. Following is the approximate brazing temperature range of the alloy:

SAE AMS4785-1968 history

• 2021 SAE AMS4785K-2021 Gold-Palladium-Nickel Alloy, Brazing Filler Metal, High Temperature 30Au - 34Pd - 36Ni 2075 to 2130 °F (1135 to 1166 °C) Solidus-Liquidus Range (UNS P00300)
• 2015 SAE AMS4785J-2015 Gold-Palladium-Nickel Alloy@ Brazing Filler Metal@ High Temperature 30Au – 34Pd – 36Ni 2075 to 2130 °F (1135 to 1166 °C) Solidus-Liquidus Range (UNS P00300)
• 2009 SAE AMS4785H-2009 Gold-Palladium-Nickel Alloy Brazing Filler Metal, High Temperature, 30Au 34Pd 36Ni, 2075 to 2130°F (1135 to 1166°C) Solidus-Liquidus Range
• 2007 SAE AMS4785G-2007 Gold-Palladium-Nickel Alloy@ Brazing Filler Metal@ High Temperature 30Au - 34Pd - 36Ni 2075 to 2130 °F (1135 to 1166 °C) Solidus-Liquidus Range (UNS P00300)
• 2002 SAE AMS4785F-2002 Gold-Palladium-Nickel Alloy, Brazing Filler Metal, High Temperature 30Au - 34Pd - 36Ni 2075 to 2130 °F (1135 to 1166 °C) Solidus-Liquidus Range
• 2001 SAE AMS4785F-2001 Gold-Palladium-Nickel Alloy Brazing Filler Metal, High Temperature, 30Au 34Pd 36Ni, 2075 to 2130°F (1135 to 1166°C) Solidus-Liquidus Range
• 1999 SAE AMS4785E-1999 Gold-Palladium-Nickel Alloy@ Brazing Filler Metal@ High Temperature 30Au - 34Pd - 36Ni 2075 to 2130 °F (1135 to 1166 °C) Solidus-Liquidus Range (UNS P00300)
• 1992 SAE AMS4785D-1992 Gold-Palladium-Nickel Alloy Brazing Filler Metal@ High Temperature 30Au - 34Pd - 36Ni 2075 to 2130 Degrees F (1135 to 1166 Degrees C) Solidus-Liquidus Range
• 1990 SAE AMS4785C-1990 BRAZING FILLER METAL@ HIGH TEMPERATURE 30Au - 34Pd - 36Ni 2075° - 2130°F (1135° - 1166°C) Solidus-Liquidus Range (UNS P00300)
• 1984 SAE AMS4785B-1984 BRAZING FILLER METAL@ HIGH TEMPERATURE 30Au - 34Pd - 36Ni 2075° - 2130°F (1135° - 1165°C) Solidus-Liquidus Range (UNS P00300)
• 1978 SAE AMS4785A-1978 BRAZING FILLER METAL@ HIGH TEMPERATURE 30Au - 34Pd - 36Ni 2075° - 2130°F (1135° - 1166°C) Solidus-Liquidus Range
• 1968 SAE AMS4785-1968 BRAZING FILLER METAL@ HIGH TEMPERATURE 30Au - 34Pd - 36Ni