SAE AMS4765E-1999
Silver Alloy, Brazing Filler Metal 56Ag 42Cu 2.0Ni 1420 to 1640 °F (771 to 893°C) Solidus-Liquidus Range

Standard No.

SAE AMS4765E-1999

Release Date

1999

Published By

Society of Automotive Engineers (SAE)

Status

Be replaced

Replace By

SAE AMS4765E-2009

Latest

SAE AMS4765G-2021

Scope

This specification covers a silver alloy in the form of wire, rod, sheet, strip, foil, pig, powder, shot, chips, and a viscous mixture (paste) of powder in a suitable binder. This material has been used typically for joining ferrous metals, particularly austenitic steels and alloys, by atmosphere furnace brazing without flux, where high joint strength up to 800 degrees F (427 degrees C) is required, or for nonferrous metals except those having base of aluminum or magnesium, but usage is not limited to such applications.

SAE AMS4765E-1999 Referenced Document

• ASTM B214-99 Standard Test Method for Sieve Analysis of Metal Powders*， 1999-04-10 Update
• ASTM E56-90 
• SAE AMS2222 TOLERANCES Copper and Copper Alloy Plate@ Sheet and Strip
• SAE AMS2222H-1994 Tolerances, Copper and Copper Alloy Sheet, Strip, and Plate
• SAE AMS2224 Tolerances Copper and Copper Alloy Wire
• SAE AMS2224F-1993 Tolerances, Copper and Copper Alloy Wire
• SAE MAM2222 Tolerances@ Metric Copper and Copper Alloy Sheet@ Strip@ and Plate
• SAE MAM2224 TOLERANCES, METRIC Copper and Copper Alloy Wire

SAE AMS4765E-1999 history

• 2021 SAE AMS4765G-2021 Silver Alloy, Brazing Filler Metal 56Ag - 42Cu - 2.0Ni 1420 to 1640 °F (771 to 893 °C) Solidus-Liquidus Range (UNS P07560)
• 2015 SAE AMS4765F-2015 Silver Alloy@ Brazing Filler Metal 56Ag - 42Cu - 2.0Ni 1420 to 1640 ��(771 to 893 �� Solidus-Liquidus Range (UNS P07560)
• 2009 SAE AMS4765E-2009 Silver Alloy, Brazing Filler Metal 56Ag - 42Cu - 2.0Ni 1420 to 1640 °F (771 to 893 °C) Solidus-Liquidus Range
• 1999 SAE AMS4765E-1999 Silver Alloy, Brazing Filler Metal 56Ag 42Cu 2.0Ni 1420 to 1640 °F (771 to 893°C) Solidus-Liquidus Range
• 1992 SAE AMS4765D-1992 Silver Alloy Brazing Filler Metal 56Ag - 42Cu - 2.0Ni 1420 to 1640 Degrees F (771 to 893 Degrees C) Solidus- Liquidus Range
• 1991 SAE AMS4765C-1991 Filler Metal@ Silver@ Brazing 56Ag - 42Cu - 2.0Ni 1420° to 1640° F (771° to 893°C) Solidus-Liquidus Range (UNS P07560)
• 1984 SAE AMS4765B-1984 Brazing Filler Metal@ Silver 56Ag - 42Cu - 2.0Ni 1420° - 1640° F (770° to 895° C) Solidus-Liquidus Range (UNS P07560)
• 1978 SAE AMS4765A-1978 Brazing Filler Metal@ Silver 56Ag - 42Cu - 2.0Ni 1420° to 1640° F (770° to 895° C) Solidus-Liquidus Range (UNS P07560)
• 1968 SAE AMS4765-1968 BRAZING FILLER METAL@ SILVER 56Ag – 42Cu – 2.0Ni