SAE AMS4765D-1992
Silver Alloy Brazing Filler Metal 56Ag - 42Cu - 2.0Ni 1420 to 1640 Degrees F (771 to 893 Degrees C) Solidus- Liquidus Range
Home
SAE AMS4765D-1992
Standard No.
SAE AMS4765D-1992
Release Date
1992
Published By
SAE - SAE International
Status
Be replaced
Replace By
SAE AMS4765E-1999
Latest
SAE AMS4765G-2021
SAE AMS4765D-1992 history
2021
SAE AMS4765G-2021
Silver Alloy, Brazing Filler Metal 56Ag - 42Cu - 2.0Ni 1420 to 1640 °F (771 to 893 °C) Solidus-Liquidus Range (UNS P07560)
2015
SAE AMS4765F-2015
Silver Alloy@ Brazing Filler Metal 56Ag - 42Cu - 2.0Ni 1420 to 1640 ��(771 to 893 �� Solidus-Liquidus Range (UNS P07560)
2009
SAE AMS4765E-2009
Silver Alloy, Brazing Filler Metal 56Ag - 42Cu - 2.0Ni 1420 to 1640 °F (771 to 893 °C) Solidus-Liquidus Range
1999
SAE AMS4765E-1999
Silver Alloy, Brazing Filler Metal 56Ag 42Cu 2.0Ni 1420 to 1640 °F (771 to 893°C) Solidus-Liquidus Range
1992
SAE AMS4765D-1992
Silver Alloy Brazing Filler Metal 56Ag - 42Cu - 2.0Ni 1420 to 1640 Degrees F (771 to 893 Degrees C) Solidus- Liquidus Range
1991
SAE AMS4765C-1991
Filler Metal@ Silver@ Brazing 56Ag - 42Cu - 2.0Ni 1420° to 1640° F (771° to 893°C) Solidus-Liquidus Range (UNS P07560)
1984
SAE AMS4765B-1984
Brazing Filler Metal@ Silver 56Ag - 42Cu - 2.0Ni 1420° - 1640° F (770° to 895° C) Solidus-Liquidus Range (UNS P07560)
1978
SAE AMS4765A-1978
Brazing Filler Metal@ Silver 56Ag - 42Cu - 2.0Ni 1420° to 1640° F (770° to 895° C) Solidus-Liquidus Range (UNS P07560)
1968
SAE AMS4765-1968
BRAZING FILLER METAL@ SILVER 56Ag – 42Cu – 2.0Ni
Copyright ©2023 All Rights Reserved