1.1 These test methods cover procedures for assessing the adhesion of relatively ductile coating films to metallic substrates by applying and removing pressure-sensitive tape over cuts made in the film.
1.2 Test Method A is primarily intended to rate the adhesion of coatings and coating systems greater than 125 µm (5 mils) in total thickness, while Test Method B is primarily intended to rate the adhesion of coatings and coating systems less than 125 µm (5 mils) in total thickness. Test Method B is not considered suitable for films thicker than 125 µm (5 mils) unless wider spaced cuts are employed and there is an explicit agreement between the purchaser and seller. If the thickness of the coating or coating system has not been predetermined, employ the use of a standard such as Practice D7091 or other appropriate standard agreed upon by interested parties prior to proceeding.
1.3 These test methods are used to evaluate whether the adhesion of a coating to a substrate is adequate for the user’s application. They do not distinguish between higher levels of adhesion for which more sophisticated methods of measurement are required.
1.4 This test method is similar in content (but not technically equivalent) to ISO 2409.
1.5 In multicoat systems adhesion failure may occur between coats so that the adhesion of the coating system to the substrate is not determined.
1.6 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.
1.7 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
1.8 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
ASTM D3359-23 Referenced Document
ASTM D1730 Standard Practices for Preparation of Aluminum and Aluminum-Alloy Surfaces for Painting
ASTM D2092 Standard Guide for Preparation of Zinc-Coated (Galvanized) Steel Surfaces for Painting
ASTM D2370 Standard Test Method for Tensile Properties of Organic Coatings
ASTM D3330/D3330M Standard Test Method for Peel Adhesion of Pressure-Sensitive Tape
ASTM D3924 Standard Specification for Standard Environment for Conditioning and Testing Paint, Varnish, Lacquer, and Related Materials
ASTM D4060 Standard Test Method for Abrasion Resistance of Organic Coatings by the Taber Abraser
ASTM D609 Standard Practice for Preparation of Cold-Rolled Steel Panels for Testing Paint, Varnish, Conversion Coatings, and Related Coating Products
ASTM D7091 Standard Practice for Nondestructive Measurement of Dry Film Thickness of Nonmagnetic Coatings Applied to Ferrous Metals and Nonmagnetic, Nonconductive Coatings Applied to Non-Ferrous Metals
ASTM D823 Standard Practices for Producing Films of Uniform Thickness of Paint, Varnish, and Related Products on Test Panels