ASTM E289-17
Standard Test Method for Linear Thermal Expansion of Rigid Solids with Interferometry

Standard No.

ASTM E289-17

Release Date

2017

Published By

American Society for Testing and Materials (ASTM)

Latest

ASTM E289-17

Scope

1.1 This test method covers the determination of linear thermal expansion of rigid solids using either a Michelson or Fizeau interferometer. 1.2 For this purpose, a rigid solid is defined as a material which, at test temperature and under the stresses imposed by instrumentation, has a negligible creep, insofar as significantly affecting the precision of thermal length change measurements. 1.3 It is recognized that many rigid solids require detailed preconditioning and specific thermal test schedules for correct evaluation of linear thermal expansion behavior for certain material applications. Since a general method of test cannot cover all specific requirements, details of this nature should be discussed in the particular material specifications. 1.4 This test method is applicable to the approximate temperature range −150°C to 700°C. The temperature range may be extended depending on the instrumentation and calibration materials used. 1.5 The precision of measurement of this absolute method (better than 640 nm/(m·K)) is significantly higher than that of comparative methods such as push rod dilatometry (for example, Test Methods D696 and E228) and thermomechanical analysis (for example, Test Method E831) techniques. It is applicable to materials having low and either positive or negative coefficients of expansion (below 5 µm/(m·K)) and where only very limited lengths or thickness of other higher expansion coefficient materials are available. 1.6 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard. 1.7 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. 1.8 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ASTM E289-17 Referenced Document

• ASTM D696 Standard Test Method for Coefficient of Linear Thermal Expansion of Plastics Between -30176C and 30176C With a Vitreous Silica Dilatometer
• ASTM E1142 Standard Terminology Relating to Thermophysical Properties
• ASTM E220 Standard Test Method for Calibration of Thermocouples By Comparison Techniques
• ASTM E228 Standard Test Method for Linear Thermal Expansion of Solid Materials With a Vitreous Silica Dilatometer
• ASTM E473 Standard Terminology Relating to Thermal Analysis
• ASTM E831 Standard Test Method for Linear Thermal Expansion of Solid Materials by Thermomechanical Analysis*， 2019-04-01 Update

ASTM E289-17 history

• 2017 ASTM E289-17 Standard Test Method for Linear Thermal Expansion of Rigid Solids with Interferometry
• 2004 ASTM E289-04(2016) Standard Test Method for Linear Thermal Expansion of Rigid Solids with Interferometry
• 2004 ASTM E289-04(2010) Standard Test Method for Linear Thermal Expansion of Rigid Solids with Interferometry
• 2004 ASTM E289-04 Standard Test Method for Linear Thermal Expansion of Rigid Solids with Interferometry
• 1999 ASTM E289-99 Standard Test Method for Linear Thermal Expansion of Rigid Solids with Interferometry