1.1 This guide describes the determination of approximate optimum SO3 for maximum performance as a result of substituting calcium sulfate for a portion of the cement.
1.2 This guide refers to the sulfur trioxide (SO3) content of the cement only. Slag cements and occasionally other hydraulic cements can contain sulfide or other forms of sulfur. The determination of SO3 content by rapid methods may include these other forms, and may therefore produce a significant error. If a significant error occurs, analyze the cement for SO3 content using the reference test method of Test Methods C114 for sulfur trioxide.
1.3 Values stated as SI units are to be regarded as standard.
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
ASTM C563-20 Referenced Document
ASTM C109/C109M Standard Test Method for Compressive Strength of Hydraulic Cement Mortars (Using 2-in. or [50-mm] Cube Specimens)
ASTM C114 Standard Test Methods for Chemical Analysis of Hydraulic Cement*, 2023-10-01 Update
ASTM C1157/C1157M Standard Performance Specification for Hydraulic Cement*, 2023-09-01 Update
ASTM C1437 Standard Test Method for Flow of Hydraulic Cement Mortar
ASTM C150/C150M Standard Specification for Portland Cement*, 2022-07-01 Update
ASTM C1679 Standard Practice for Measuring Hydration Kinetics of Hydraulic Cementitious Mixtures Using Isothermal Calorimetry*, 2022-12-15 Update
ASTM C1702 Standard Test Method for Measurement of Heat of Hydration of Hydraulic Cementitious Materials Using Isothermal Conduction Calorimetry*, 2023-08-01 Update
ASTM C192/C192M Standard Practice for Making and Curing Concrete Test Specimens in the Laboratory
ASTM C204 Standard Test Methods for Fineness of Hydraulic Cement by Air-Permeability Apparatus
ASTM C305 Standard Practice for Mechanical Mixing of Hydraulic Cement Pastes and Mortars of Plastic Consistency
ASTM C39/C39M Standard Test Method for Compressive Strength of Cylindrical Concrete Specimens
ASTM C430 Standard Test Method for Fineness of Hydraulic Cement by the 45-956;m (No. 325) Sieve
ASTM C465 Standard Specification for Processing Additions for Use in the Manufacture of Hydraulic Cements
ASTM C471M Standard Test Methods for Chemical Analysis of Gypsum and Gypsum Products [Metric]
ASTM C595/C595M Standard Specification for Blended Hydraulic Cements*, 2023-07-15 Update
ASTM C596 Standard Test Method for Drying Shrinkage of Mortar Containing Hydraulic Cement
ASTM C78/C78M Standard Test Method for Flexural Strength of Concrete (Using Simple Beam with Third-Point Loading)*, 2022-03-01 Update
ASTM C563-20 history
2020ASTM C563-20 Standard Guide for Approximation of Optimum SO3 in Hydraulic Cement
2019ASTM C563-19 Standard Guide for Approximation of Optimum SO3 in Hydraulic Cement
2018ASTM C563-18a Standard Guide for Approximation of Optimum SO3 in Hydraulic Cement
2018ASTM C563-18 Standard Guide for Approximation of Optimum SO3 in Hydraulic Cement
2017ASTM C563-17 Standard Guide for Approximation of Optimum SO3 in Hydraulic Cement
2016ASTM C563-16 Standard Guide for Approximation of Optimum SO3 in Hydraulic Cement Using Compressive Strength
2015ASTM C563-15 Standard Test Method for Approximation of Optimum SO3 in Hydraulic Cement Using Compressive Strength
2013ASTM C563-13 Standard Test Method for Approximation of Optimum SO3 in Hydraulic Cement Using Compressive Strength
2007ASTM C563-07 Standard Test Method for Approximation of Optimum SO3 in Hydraulic Cement Using Compressive Strength
2004ASTM C563-04 Standard Test Method for Optimum SO3 in Hydraulic Cement Using 24-h Compressive Strength
2003ASTM C563-03 Standard Test Method for Optimum SO3 in Hydraulic Cement Using 24-h Compressive Strength
2002ASTM C563-02 Standard Test Method for Optimum SO3 in Hydraulic Cement Using 24-h Compressive Strength
1996ASTM C563-96 Standard Test Method for Optimum SO3 in Hydraulic Cement Using 24-h Compressive Strength