1.1 This specification covers hot-applied crack filler for use in filling cracks in asphalt concrete and portland cement concrete pavements.
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
ASTM D5078/D5078M-11(2021) Referenced Document
ASTM D217 Standard Test Methods for Cone Penetration of Lubricating Grease
ASTM D36/D36M Standard Test Method for Softening Point of Bitumen &40;Ring-and-Ball Apparatus&41;*, 2024-04-20 Update
ASTM D5/D5M Standard Test Method for Penetration of Bituminous Materials
ASTM D5167 Standard Practice for Melting of Hot-Applied Joint and Crack Sealant and Filler for Evaluation
ASTM D5329 Standard Test Methods for Sealants and Fillers, Hot-Applied, For Joints and Cracks in Asphaltic and Portland Cement Concrete Pavements
ASTM D5078/D5078M-11(2021) history
2021ASTM D5078/D5078M-11(2021) Standard Specification for Crack Filler, Hot-Applied, for Asphalt Concrete and Portland Cement Concrete Pavements
2011ASTM D5078/D5078M-11(2016) Standard Specification for Crack Filler, Hot-Applied, for Asphalt Concrete and Portland Cement Concrete Pavements
2011ASTM D5078/D5078M-11 Standard Specification for Crack Filler, Hot-Applied, for Asphalt Concrete and Portland Cement Concrete Pavements
1995ASTM D5078-95(2006) Standard Specification for Crack Filler, Hot-Applied, for Asphalt Concrete and Portland Cement Concrete Pavements
1995ASTM D5078-95(2000) Standard Specification for Crack Filler, Hot-Applied, for Asphalt Concrete and Portland Cement Concrete Pavements