ASTM E2347-21
Standard Test Method for Indentation Softening Temperature by Thermomechanical Analysis
- Standard No.
- ASTM E2347-21
- Release Date
- 2021
- Published By
- American Society for Testing and Materials (ASTM)
- Latest
- ASTM E2347-21
- Scope
- 1.1?This test method is applicable to high modulus materials that soften upon heating to a modulus less than 6.0 MPa. This test method describes the determination of the temperature at which the specific modulus of either 6.65 MPa (Method A) or 33.3 MPa (Method B) (equivalent to
ASTM E2347-21 Referenced Document
- ASTM D1525 Standard Test Method for Vicat Softening Temperature of Plastics
- ASTM E1142 Standard Terminology Relating to Thermophysical Properties
- ASTM E1363 Standard Test Method for Temperature Calibration of Thermomechanical Analyzers
- ASTM E2113 Standard Test Method for Length Change Calibration of Thermomechanical Analyzers
- ASTM E2206 Standard Test Method for Force Calibration of Thermomechanical Analyzers
- ASTM E473 Standard Terminology Relating to Thermal Analysis
ASTM E2347-21 history
- 2021 ASTM E2347-21 Standard Test Method for Indentation Softening Temperature by Thermomechanical Analysis
- 2016 ASTM E2347-16 Standard Test Method for Indentation Softening Temperature by Thermomechanical Analysis
- 2011 ASTM E2347-11 Standard Test Method for Indentation Softening Temperature by Thermomechanical Analysis
- 2005 ASTM E2347-05 Standard Test Method for Indentation Softening Temperature by Thermomechanical Analysis
- 2004 ASTM E2347-04 Standard Test Method for Indentation Softening Temperature by Thermomechanical Analysis