ASTM D1824-16 PDF

Scope: 4.1 The suitability of a dispersion resin for any given application process is dependent upon its viscosity characteristics.

4.2 The viscosity defines the flow behavior of a plastisol or organosol under low shear. This viscosity relates to the conditions encountered in pouring, casting, molding, and dipping processes.

1.1 This test method covers the measurement of plastisol and organosol viscosity at low shear rates.

1.2 Apparent viscosity at high shear rates is covered in Test Method D1823.

1.3 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.

1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

Note 1: This test method resembles ISO 3219-1977 in title only. The content is significantly different.

ASTM D1824-16 Referenced Document

ASTM D1755 Standard Specification for Poly(Vinyl Chloride) Resins
ASTM D1823 Standard Test Method for Apparent Viscosity of Plastisols and Organosols at High Shear Rates by Extrusion Viscometer
ASTM E1 Standard Specification for ASTM Thermometers
ASTM E691 Standard Practice for Conducting an Interlaboratory Study to Determine the Precision of a Test Method

2016 ASTM D1824-16 Standard Test Method for Apparent Viscosity of Plastisols and Organosols at Low Shear Rates
2010 ASTM D1824-95(2010) Standard Test Method for Apparent Viscosity of Plastisols and Organosols at Low Shear Rates
1995 ASTM D1824-95(2002) Standard Test Method for Apparent Viscosity of Plastisols and Organosols at Low Shear Rates
1995 ASTM D1824-95 Standard Test Method for Apparent Viscosity of Plastisols and Organosols at Low Shear Rates
1980 ASTM D1824-66(1980)e1 Standard Test Method for Apparent Viscosity Of Plastisols And Organosols At Low Shear Rates By Brookfield Viscometer
1972 ASTM D1824-66(1972) Standard Method Of Test For Apparent Viscosity Of Plastisols And Organosols At Low Shear Rates By Brookfield Viscometer