ASTM G139-05(2015)
Standard Test Method for Determining Stress-Corrosion Cracking Resistance of Heat-Treatable Aluminum Alloy Products Using Breaking Load Method

Standard No.

ASTM G139-05(2015)

Release Date

2005

Published By

American Society for Testing and Materials (ASTM)

Status

Be replaced

Replace By

ASTM G139-05(2022)

Latest

ASTM G139-05(2022)

Scope

5.1 The test method was developed for use with high strength aluminum alloys (2XXX and Cu containing 7XXX) that are normally tested in 3.5 weight % NaCl by alternate immersion. However, the concept which uses residual strength as a measure of damage evolution (in this case environmentally-assisted cracking) can, in principle, be applied to any alloy and environmental system.

5.2 This test method has been developed for research studies of alloys and tempers with improved resistance to SCC. The test results permit different material variants to be compared with a high degree of confidence and with much more precision than the results of pass/fail tests. Thus, it is particularly useful for comparing materials with similar levels of resistance to stress-corrosion cracking. The procedure could be modified for use as a quality assurance tool but this has not been a primary purpose during its development.

5.3 The exposure periods and conditions that are described in this test method apply specifically to high strength aluminum alloys, but the statistical techniques should be valid for other alloy systems with different exposure conditions.

5.4 Although this particular procedure was primarily intended for testing products in the short-transverse stressing direction, it is useful for other stressing directions, particularly the long-transverse direction in sheet and thin plate products.

5.5 Determination of the actual serviceability of a material requires stress-corrosion testing performed in the intended service environment, under conditions relating to the end use, including protective measures such as coatings and inhibitors and is outside the scope of this test method.

5.5.1 There is no good way to compare test environments to actual service because most service environments have large inherent variability with respect to a single structure that may experience many different environments or with respect to two identical structures that serve in different locations. Unless a sample can be tested in the actual service environment for the expected life of the component, no conclusive determination can be made about the suitability of a particular material for a particular application. Designers must therefore make judgments on the suitability of particular materials for applications based on knowledge of the material and of the service environment. To avoid service failures, the environment used for preliminary evaluations is often chosen based on a worst case scenario leading to intentional overestimations of corrosion damage.

1.1 This test method covers procedures for evaluation of stress corrosion cracking (SCC) resistance by the breaking load test method, a concept which uses residual strength as the measure of damage evolution (in this case environmentally assisted cracking).

1.2 This test method covers specimen type and replication, test environment, stress levels, exposure periods, final strength determination, and statistical analysis of the raw residual strength data.

1.3 The test method was developed for use with heat-treatab......

ASTM G139-05(2015) Referenced Document

• ASTM E691 Standard Practice for Conducting an Interlaboratory Study to Determine the Precision of a Test Method
• ASTM E8 Standard Test Methods for Tension Testing of Metallic Materials
• ASTM G44 Standard Practice for Exposure of Metals and Alloys by Alternate Immersion in Neutral 3.5?% Sodium Chloride Solution
• ASTM G47 Standard Test Method for Determining Susceptibility to Stress-Corrosion Cracking of 2XXX and 7XXX Aluminum Alloy Products
• ASTM G49 Standard Practice for Preparation and Use of Direct Tension Stress-Corrosion Test Specimens
• ASTM G64 Standard Classification of Resistance to Stress-Corrosion Cracking of Heat-Treatable Aluminum Alloys

ASTM G139-05(2015) history

• 2022 ASTM G139-05(2022) Standard Test Method for Determining Stress-Corrosion Cracking Resistance of Heat-Treatable Aluminum Alloy Products Using Breaking Load Method
• 2005 ASTM G139-05(2015) Standard Test Method for Determining Stress-Corrosion Cracking Resistance of Heat-Treatable Aluminum Alloy Products Using Breaking Load Method
• 2005 ASTM G139-05(2011) Standard Test Method for Determining Stress-Corrosion Cracking Resistance of Heat-Treatable Aluminum Alloy Products Using Breaking Load Method
• 2005 ASTM G139-05 Standard Test Method for Determining Stress-Corrosion Cracking Resistance of Heat-Treatable Aluminum Alloy Products Using Breaking Load Method
• 1996 ASTM G139-96 Standard Test Method for Determining Stress-Corrosion Cracking Resistance of Heat-Treatable Aluminum Alloy Products Using Breaking Load Method