ASTM D5519-15
Standard Test Methods for Particle Size Analysis of Natural and Man-Made Riprap Materials

Standard No.

ASTM D5519-15

Release Date

2015

Published By

American Society for Testing and Materials (ASTM)

Latest

ASTM D5519-15

Scope

5.1 Riprap is commonly used to prevent erosion of underlying materials due to the effects of rain runoff, wind, flowing water, or wave action. The particle size distribution (mass of particles) is an important physical characteristic of riprap, as discussed in Guide D6825. These test methods provide a gradation of the material graphically represented as percent finer than the particle mass. If a gradation can be established or accepted on the basis of only maximum and minimum particle sizes, then it may not be necessary to establish the complete gradation in accordance with these test methods.

5.2 These test methods can be used during evaluation of a potential source, as a means of product acceptance, or for assessment of existing installations. Method D is not recommended as a means of product acceptance.

5.3 Other characteristics of interest, such as particle shape, particle angularity, or visually evident rock durability characteristics may be determined during the performance of these test methods.

5.4 Interpretation of test results must consider the representativeness of the sample.

Note 2: The quality of the result produced by this standard is dependent upon the competence of the personnel performing it, and the suitability of the equipment and facilities used. Agencies that meet the criteria of Practice D3740 are generally considered capable of competent and objective testing/sampling/inspection/etc. Users of this standard are cautioned that compliance with Practice D3740 does not in itself ensure reliable results. Reliable results depend on many factors; Practice D3740 provides a means of evaluating some of those factors.

1.1 These test methods cover the particle size and mass analysis of natural and man-made riprap and related materials, including filter stone or coarse bedding materials.

1.2 These test methods are generally intended for riprap and related materials. They are applicable for mixtures of stones screened from natural deposits, blast rock, processed materials from quarried rock, or recycled concrete. They are applicable for sizes 3 in. (75 mm) and above, with the upper size limited only by equipment available for handling and determining the mass of the individual particles.

1.3 Four alternate procedures are provided. There is a wide range in the level of effort and the precision of the test procedures. It is important for specifiers to indicate the test procedure. Test reports should clearly indicate which procedure was used.

Note 1: While conducting these test methods, it may be convenient to collect data on other attributes, such as the amount of slab pieces and deleterious materials.

1.4 All observed and calculated values shall......

ASTM D5519-15 Referenced Document

• ASTM C136 Standard Test Method for Sieve Analysis of Fine and Coarse Aggregates
• ASTM D3740 Standard Practice for Minimum Requirements for Agencies Engaged in the Testing and/or Inspection of Soil and Rock as Used in Engineering Design and Construction
• ASTM D4992 Standard Practice for Evaluation of Rock to be Used for Erosion Control
• ASTM D5240 Standard Test Method for Testing Rock Slabs to Evaluate Soundness of Riprap by Use of Sodium Sulfate or Magnesium Sulfate
• ASTM D5312 Standard Test Method for Evaluation of Durability of Rock for Erosion Control Under Freezing and Thawing Conditions
• ASTM D5313 Standard Test Method for Evaluation of Durability of Rock for Erosion Control Under Wetting and Drying Conditions
• ASTM D6026 Standard Practice for Using Significant Digits in Geotechnical Data
• ASTM D653 Standard Terminology Relating to Soil, Rock, and Contained Fluids
• ASTM D6825 Standard Guide for Placement of Riprap Revetments
• ASTM E11 Standard Specification for Wire Cloth and Sieves for Testing Purposes

ASTM D5519-15 history

• 2015 ASTM D5519-15 Standard Test Methods for Particle Size Analysis of Natural and Man-Made Riprap Materials
• 2014 ASTM D5519-14 Standard Test Methods for Particle Size Analysis of Natural and Man-Made Riprap Materials
• 2007 ASTM D5519-07 Standard Test Methods for Particle Size Analysis of Natural and Man-Made Riprap Materials
• 1994 ASTM D5519-94(2001) Standard Test Method for Particle Size Analysis of Natural and Man-Made Riprap Materials
• 1994 ASTM D5519-94 Standard Test Method for Particle Size Analysis of Natural and Man-Made Riprap Materials