ASTM D7998-15
Standard Test Method for Measuring the Effect of Temperature on the Cohesive Strength Development of Adhesives using Lap Shear Bonds under Tensile Loading

Standard No.

ASTM D7998-15

Release Date

2015

Published By

American Society for Testing and Materials (ASTM)

Status

Be replaced

Replace By

ASTM D7998-19

Latest

ASTM D7998-19

Scope

4.1 The test method enables strength values for wood and other materials bonded with an adhesive under a range of controlled bonding temperature, time, and pressure conditions to be evaluated. Bond formation and subsequent testing is affected in a coordinated fashion, and this enables transient strength values of sets of similar bond types to be explored with diverse parameters as independent variables. Principal among these variables is the temperature at which bonds are formed and the time that selected temperatures are maintained prior to testing. The use of controlled methods of adhesive application, the rapid attainment of stable bond formation conditions, and the rapid transition to the bond testing mode enables snapshots of bond strength to be attained as bonds progress from limited strength (or initial tack) to maximum strength. Derived data may be used to evaluate and compare the strength development characteristics of diverse types and formulations of adhesive. The method may thus be used to aid in tailoring and matching adhesives to the manufacture of diverse bonded products that involve heating.

4.2 The method may also be used to evaluate the co-dependent effect of temperature and time on the degradation of sample bonds. Pressing temperatures up to 265°C (509°F) may be necessary for such investigations of thermal degradation. Specimens are pressed for a range of times and temperatures and very shortly thereafter tested either at elevated temperature or immediately following rapid forced air cooling. Alternatively, thermal damage of pre-formed bond samples may be evaluated by subjecting them to controlled temperature and time sequences prior to testing.

4.3 The method may also be used to evaluate the effect of wood type and variability, or of non-wood materials, on bond strength development.

4.4 By hermetically sealing the overlap region of sample bonds during their formation, the method may also be used to evaluate the effect of moisture and other resident volatile fluids on bond strength development.

4.5 The method may also be used to evaluate the effect that the temperature at which variously formed bonds are tested has on their strength. Controlled rapid forced air cooling immediately after bond formation but before testing is necessary for such investigations. This approach may be employed to explore the thermoplastic characteristic of thermosetting adhesives and also the strength of hot melt adhesives as a function of pressing and testing temperatures.

1.1 This test method concerns bonding and testing of wood adhesives and related adhesives using small scale tensile lap-shear samples in a manner that emphasizes transient cohesive strength as a function of bonding time and temperature.

1.2 Use of thin adherends enables bondlines to be rapidly heated to elevated temperatures and maintained at those temperatures for a range of times at a controlled pressure before testing.

1.3 Optional rapid forced air cooling of bonds after pressing and immediately before testing enables the effect of testing temperature on transient strength to......

ASTM D7998-15 Referenced Document

• ASTM D907 Standard Terminology of Adhesives

ASTM D7998-15 history

• 2019 ASTM D7998-19 Standard Test Method for Measuring the Effect of Temperature on the Cohesive Strength Development of Adhesives using Lap Shear Bonds under Tensile Loading
• 2015 ASTM D7998-15 Standard Test Method for Measuring the Effect of Temperature on the Cohesive Strength Development of Adhesives using Lap Shear Bonds under Tensile Loading