ASTM B699-86(2015)
Standard Specification for Coatings of Cadmium Vacuum-Deposited on Iron and Steel
- Standard No.
- ASTM B699-86(2015)
- Release Date
- 1986
- Published By
- American Society for Testing and Materials (ASTM)
- Status
- Replace By
- ASTM B699-86(2021)
- Latest
- ASTM B699-86(2021)e1
- Scope
1.1 This specification covers the requirements for a cadmium coating vacuum-deposited on iron and steel basis metals. The coating is especially beneficial to those ferrous metals, heat treated to 46HRC and higher or having an ultimate tensile strength greater than 1500 MPa, wherein protection against corrosion and appearance are important (see Appendix X1).
1.2 Vacuum-deposited production items are normally free of hydrogen embrittlement, a danger when using electroplating processes for deposition. Vacuum deposition can handle large high-strength parts that cannot be conveniently mechanically plated in the rotating barrels.
1.3 The coating is provided in various thicknesses up to and including 12 μm (3.1) either in the as-deposited condition or with a supplementary finish (3.2).
1.4 8201;The following precautionary caveat pertains only to the test methods portion, Section 9, of this specification: This standard does not purport to address all of the safety problems, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.
ASTM B699-86(2015) Referenced Document
- ASTM B117 Standard Practice for Operating Salt Spray (Fog) Apparatus*， 1997-04-10 Update
- ASTM B183 Standard Practice for Preparation of Low-Carbon Steel for Electroplating
- ASTM B201 Standard Practice for Testing Chromate Coatings on Zinc and Cadmium Surfaces*， 2019-04-01 Update
- ASTM B242 Standard Guide for Preparation of High-Carbon Steel for Electroplating*， 2020-11-01 Update
- ASTM B254 Standard Practice for Preparation of and Electroplating on Stainless Steel*， 2020-11-01 Update
- ASTM B320 Standard Practice for Preparation of Iron Castings for Electroplating*， 2019-04-01 Update
- ASTM B322 Standard Guide for Cleaning Metals Prior to Electroplating*， 2020-11-01 Update
- ASTM B440 Standard Specification for Cadmium*， 2021-11-01 Update
- ASTM B487 Standard Test Method for Measurement of Metal and Oxide Coating Thickness by Microscopical Examination of Cross Section
- ASTM B499 Standard Test Method for Measurement of Coating Thicknesses by the Magnetic Method: Nonmagnetic Coatings on Magnetic Basis Metals*， 1996-04-20 Update
- ASTM B504 Standard Test Method for Measurement of Thickness of Metallic Coatings by the Coulometric Method*， 2023-05-01 Update
- ASTM B567 Standard Test Method for Measurement of Coating Thickness by the Beta Backscatter Method*， 2024-04-20 Update
- ASTM B568 Standard Test Method for Measurement of Coating Thickness by X-Ray Spectrometry*， 2021-04-01 Update
- ASTM B571 Standard Practice for Qualitative Adhesion Testing of Metallic Coatings*， 1997-04-20 Update
- ASTM B602 Standard Test Method for Attribute Sampling of Metallic and Inorganic Coatings*， 1988-04-20 Update
- ASTM B697 Standard Guide for Selection of Sampling Plans for Inspection of Electrodeposited Metallic and Inorganic Coatings*， 2021-10-01 Update
- ASTM E396 Standard Test Methods for Chemical Analysis of Cadmium*， 1998-05-10 Update
- ASTM F519 Standard Test Method for Mechanical Hydrogen Embrittlement Evaluation of Plating Processes and Service Environments*， 2000-06-26 Update
ASTM B699-86(2015) history
- 2021 ASTM B699-86(2021)e1 Standard Specification for Coatings of Cadmium Vacuum-Deposited on Iron and Steel
- 2021 ASTM B699-86(2021) Standard Specification for Coatings of Cadmium Vacuum-Deposited on Iron and Steel
- 1986 ASTM B699-86(2015) Standard Specification for Coatings of Cadmium Vacuum-Deposited on Iron and Steel
- 1986 ASTM B699-86(2008) Standard Specification for Coatings of Cadmium Vacuum-Deposited on Iron and Steel
- 1986 ASTM B699-86(2003) Standard Specification for Coatings of Cadmium Vacuum-Deposited on Iron and Steel
- 1998 ASTM B699-86(1998) Standard Specification for Coatings of Cadmium Vacuum-Deposited on Iron and Steel