ASTM E423-71(2014)
Standard Test Method for Normal Spectral Emittance at Elevated Temperatures of Nonconducting Specimens

Standard No.

ASTM E423-71(2014)

Release Date

1971

Published By

American Society for Testing and Materials (ASTM)

Status

Be replaced

Replace By

ASTM E423-71(2019)

Latest

ASTM E423-71(2019)

Scope

5.1 The significant features are typified by a discussion of the limitations of the technique. With the description and arrangement given in the following portions of this test method, the instrument will record directly the normal spectral emittance of a specimen. However, the following conditions must be met within acceptable tolerance, or corrections must be made for the specified conditions.

5.1.1 The effective temperatures of the specimen and blackbody must be within 1 K of each other. Practical limitations arise, however, because the temperature uniformities are often not better than a few kelvins.

5.1.2 The optical path length in the two beams must be equal, or, preferably, the instrument should operate in a nonabsorbing atmosphere, in order to eliminate the effects of differential atmospheric absorption in the two beams. Measurements in air are in many cases important, and will not necessarily give the same results as in a vacuum, thus the equality of the optical paths for dual-beam instruments becomes very critical.

Note 4—Very careful optical alignment of the spectrophotometer is required to minimize differences in absorptance along the two paths of the instrument, and careful adjustment of the chopper timing to reduce “cross-talk” (the overlap of the reference and sample signals) as well as precautions to reduce stray radiation in the spectrophotometer are required to keep the zero line flat. With the best adjustment, the “100 % line” will be flat to within 3 %.

5.1.3 Front-surface mirror optics must be used throughout, except for the prism in prism monochromators, and it should be emphasized that equivalent optical elements must be used in the two beams in order to reduce and balance attenuation of the beams by absorption in the optical elements. It is recommended that optical surfaces be free of SiO₂ and SiO coatings: MgF₂ may be used to stabilize mirror surfaces for extended periods of time. The optical characteristics of these coatings are critical, but can be relaxed if all optical paths are fixed during measurements or the incident angles are not changed between modes of operation (during 0 % line, 100 % line, and sample measurements). It is recommended that all optical elements be adequately filled with energy.

5.1.4 The source and field apertures of the two beams must be equal in order to ensure that radiant flux in the two beams compared by the apparatus will pertain to equal areas of the sources and equal solid angles of emission. In some cases it may be desirable to define the solid angle of the source and sample when comparing alternative measurement techniques.

5.1.5 The response of the detector-amplifier system must vary linearly with the incident radiant flux, or must be calibrated for linearity, and corrections made for observed deviations from linearity.

1.1 This test method describes an accurate technique for measuring the normal spectral emittance of electrically nonconducting materials in the temperature range from 1000 to 1800 K, and at wavelengths from 1 to 35 μm. It is particularly suitable for measuring the normal spectral emittance of materials such as ceramic oxides, which have relatively low thermal conductivity and are translucent to appreciable depths (several millimetres) below the surface, but which become essent......

ASTM E423-71(2014) Referenced Document

• ASTM E349 Standard Terminology Relating to Space Simulation*， 2019-10-01 Update

ASTM E423-71(2014) history

• 2019 ASTM E423-71(2019) Standard Test Method for Normal Spectral Emittance at Elevated Temperatures of Nonconducting Specimens
• 1971 ASTM E423-71(2014) Standard Test Method for Normal Spectral Emittance at Elevated Temperatures of Nonconducting Specimens
• 1971 ASTM E423-71(2008) Standard Test Method for Normal Spectral Emittance at Elevated Temperatures of Nonconducting Specimens
• 1971 ASTM E423-71(2002) Standard Test Method for Normal Spectral Emittance at Elevated Temperatures of Nonconducting Specimens
• 1971 ASTM E423-71(1996)e1 Standard Test Method for Normal Spectral Emittance at Elevated Temperatures of Nonconducting Specimens