SAE AMS4161H-2013
Aluminum Alloy, Extrusions 1.0Mg 0.60Si 0.28Cu 0.20Cr (6061-T4) Solution Heat Treated and Naturally Aged
Home
SAE AMS4161H-2013
Standard No.
SAE AMS4161H-2013
Release Date
2013
Published By
Society of Automotive Engineers (SAE)
Status
Be replaced
Replace By
SAE AMS4161J-2020
Latest
SAE AMS4161J-2020
Scope
This specification covers an aluminum alloy in the form of extruded bars, rods, wire, shapes, and tubing.
SAE AMS4161H-2013 Referenced Document
ASTM B594-09
Standard Practice for Ultrasonic Inspection of Aluminum-Alloy Wrought Products for Aerospace Applications
*
,
2024-04-20 Update
ASTM B594-13
Standard Practice for Ultrasonic Inspection of Aluminum-Alloy Wrought Products
*
,
2024-04-20 Update
ASTM B660-08
Standard Practices for Packaging/Packing of Aluminum and Magnesium Products
*
,
2024-04-20 Update
ASTM B666/B666M-08
Standard Practice for Identification Marking of Aluminum and Magnesium Products
*
,
2024-04-20 Update
ASTM B807-02
Standard Practice for Extrusion Press Solution Heat Treatment for Aluminum Alloys
ASTM B807/B807M-06
Standard Practice for Extrusion Press Solution Heat Treatment for Aluminum Alloys
*
,
2024-04-20 Update
SAE AMS2355
TENSILE TESTING OF WROUGHT ALUMINUM AND MAGNESIUM PRODUCTS Except Forgings
SAE AMS2772-1997
Heat Treatment of Aluminum Alloy Raw Materials (01 1997)
SAE AS1990-1990
Aluminum Alloy Tempers
SAE AMS4161H-2013 history
2020
SAE AMS4161J-2020
Aluminum Alloy, Extrusions 1.0Mg - 0.60Si - 0.28Cu - 0.20Cr (6061-T4) Solution Heat Treated and Naturally Aged
2013
SAE AMS4161H-2013
Aluminum Alloy, Extrusions 1.0Mg 0.60Si 0.28Cu 0.20Cr (6061-T4) Solution Heat Treated and Naturally Aged
2011
SAE AMS4161E-2011
ALUMINUM ALLOY EXTRUSIONS 1.0Mg - 0.60Si - 0.28Cu - 0.20Cr (6061-T4) Solution Heat Treated and Naturally Aged
2010
SAE AMS4161G-2010
Aluminum Alloy, Extrusions 1.0Mg - 0.60Si - 0.28Cu - 0.20Cr (6061-T4) Solution Heat Treated and Naturally Aged
2002
SAE AMS4161G-2002
Aluminum Alloy, Extrusions 1.0Mg 0.60Si 0.28Cu 0.20Cr (6061-T4) Solution Heat Treated and Naturally Aged
1996
SAE AMS4161F-1996
Aluminum Alloy@ Extrusions 1.0Mg - 0.60Si - 0.28Cu - 0.20Cr (6061-T4) Solution Heat Treated and Naturally Aged (UNS A96061)
1991
SAE AMS4161E-1991
Aluminum Alloy@ Extrusions 1.0Mg - 0.60Si - 0.28Cu - 0.20Cr (6061-T4) Solution Heat Treated and Naturally Aged (UNS A96061)
1984
SAE AMS4161D-1984
ALUMINUM ALLOY EXTRUSIONS 1.0Mg - 0.60Si - 0.28Cu - 0.20Cr (6061-T4) Solution Heat Treated and Naturally Aged
1978
SAE AMS4161C-1978
ALUMINUM ALLOY EXTRUSIONS 1.0Mg - 0.60Si - 0.30Cu - 0.20Cr (6061-T4)
1968
SAE AMS4161B-1968
ALUMINUM ALLOY EXTRUSIONS 1.0Mg - 0.60Si - 0.30Cu - 0.20Cr (6061-T4)
1966
SAE AMS4161A-1966
ALUMINUM ALLOY EXTRUSIONS 1.0Mg - 0.60Si - 0.30Cu - 0.20Cr (6061-T4)
1960
SAE AMS4161-1960
ALUMINUM ALLOY EXTRUSIONS 1Mg - 0.6Si - 0.25Cu - 0.25Cr (6061-T4)
Copyright ©2024 All Rights Reserved