ASTM D1053-92a(2012)
Standard Test Methods for Rubber Propertymdash;Stiffening at Low Temperatures: Flexible Polymers and Coated Fabrics

Standard No.

ASTM D1053-92a(2012)

Release Date

1992

Published By

American Society for Testing and Materials (ASTM)

Status

Be replaced

Replace By

ASTM D1053-92a(2018)

Latest

ASTM D1053-92a(2018)

Scope

4.1 These test methods may be used to determine the subnormal temperature stiffening of flexible polymers or fabrics coated with flexible polymers. Temperatures at which the low temperature modulus is a specified multiple or ratio of the modulus at room temperature are interpolated from the twist versus temperature curve. These specified ratios of low-temperature modulus to room-temperature modulus are called relative moduli. These temperatures at the relative moduli encompass the transition region between the glassy and rubbery states of the materials tested.

A8201;Torsion head	G8201;Movable protractor
B8201;Torsion wire	H8201;Supporting stand
C8201;Sieve	I8201;Specimen rack
D8201;Clamp stud	J8201;Test specimen
E8201;Screw connector	K8201;Bottom clamp
F8201;Pointer	L8201;Top clamp

FIG. 1 Schematic Drawing of Apparatus for Low-Temperature Stiffness Test

4.2 These test methods offer only a general guide to stiffness characterization as service conditions of experimental materials may differ greatly from the test conditions.

1.1 These test methods describe the use of a torsional apparatus for measuring the relative low temperature stiffening of flexible polymeric materials and fabrics coated therewith. A routine inspection and acceptance procedure, to be used as a pass-fail test at a specified temperature, is also described.

1.2 These test methods yield comparative data to assess the low temperature performance of flexible polymers and fabrics coated therewith.

1.3 The values stated in SI units are to be regarded as standard. The values given in parentheses are for information only.

1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practice......

ASTM D1053-92a(2012) Referenced Document

• ASTM D4483 Standard Practice for Determining Precision for Test Method Standards in the Rubber and Carbon Black Industries*， 1999-04-20 Update
• ASTM D832 Standard Practice for Rubber Conditioning For Low-Temperature Testing

ASTM D1053-92a(2012) history

• 2018 ASTM D1053-92a(2018) Standard Test Methods for Rubber Property—Stiffening at Low Temperatures: Flexible Polymers and Coated Fabrics
• 1992 ASTM D1053-92a(2012) Standard Test Methods for Rubber Propertymdash;Stiffening at Low Temperatures: Flexible Polymers and Coated Fabrics
• 1992 ASTM D1053-92a(2007) Standard Test Methods for Rubber Property-Stiffening at Low Temperatures: Flexible Polymers and Coated Fabrics
• 1992 ASTM D1053-92a(2001)e1 Standard Test Methods for Rubber Property—Stiffening at Low Temperatures Flexible Polymers and Coated Fabrics
• 1992 ASTM D1053-92a(1997) Standard Test Methods for Rubber Property8212;Stiffening at Low Temperatures: Flexible Polymers and Coated Fabrics