For purpose of determining compliance with the specified limits for requirements of the properties listed in the following table, an observed value or a calculated value shall be rounded as indicated in accordance with Practice E29.
| Property | Unit | Rounded Unit for Observed or Calculated Value | |
|---|---|---|---|
| Chemical composition | percent | ||
| Hardness Knoop (100-g load unless other- wise specified) Vicker (specify load) Rockwell (all scales, specify which) Rockwell superficial (all scales, specify which) | nearest unit on the last right hand place of figure of specified limit | ||
| Resistivity | μΩ·cm | ||
| Tensile strength | psi (MPa) | nearest 1000 psi (nearest 10 MPa) | |
| Yield Strength | psi (MPa) | nearest 1000 psi (nearest 10 MPa) | |
| Elongation | |||
| Below 5 % | percent | nearest multiple of 0.5 % | |
| 5 % and over | percent | nearest 1 % | |
| Grain size | |||
| Up to 0.055 mm incl. | mm | nearest multiple of 0.005 mm | |
| Over 0.055 to 0.160, mm, incl. | mm | nearest 0.01 mm | |
1.1 This specification covers general requirements common to wrought precious metal electrical contact alloy products in the form of sheet, strip, wire, and rod. Unless otherwise specified in the purchase order or in an individual specification, these general requirements shall apply to wrought electrical contact materials where indicated in the applicable product specifications issued by ASTM.
1.2 In case of conflict, the requirements on the purchase order, the individual specification, and this general specification shall prevail in the sequence named.
1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.
1.4 This standard does not purport ......