ASTM D6105-04(2012)
Standard Practice for Application of Electrical Discharge Surface Treatment (Activation) of Plastics for Adhesive Bonding

Standard No.

ASTM D6105-04(2012)

Release Date

2004

Published By

American Society for Testing and Materials (ASTM)

Status

Be replaced

Replace By

ASTM D6105-04(2019)

Latest

ASTM D6105-04(2019)

Scope

Bonding of many polymeric substrates presents a problem due to the low wettability of their surfaces and their chemical inertness. Adhesive bond formation begins with the establishment of interfacial molecular contact by wetting. Wettability of a substrate surface depends on its surface energy. The surface activation with electrical discharges improves wettability of polymers and subsequent adhesive bonding. The surface activation with electrical discharges results in addition of polar functional groups on the polymer surface. The higher the concentration of polar functional groups on the surface the more actively the surface reacts with the different polar interfaces.

To achieve a proper adhesive bond the polyolefin substrate's polar component should be raised from near zero to 15 to 20 mJ/m².

The pre-treated surfaces are ready for application of the adhesive immediately after the treatment.

1.1 This practice covers various electrical discharge treatments to be used to enhance the ability of polymeric substrates to be adhesively bonded. This practice does not include additional information on the preparation of test specimens or testing conditions as they are covered in the various ASTM test methods or specifications for specific materials.

1.2 The types of discharge phenomena that are used for surface modification of polymers fit into the general category of nonequilibrium or non-thermal discharges in which electron temperature (mean energy) greatly exceeds the gas temperature.

1.3 The technologies included in this practice are:

Technology	Section
Gas plasma at reduced pressure	8
Electrical discharges at atmospheric pressure	9
AC dielectric barrier discharge	9.1
High Frequency Apparatus	9.1.1
Suppressed Spark Apparatus	9.1.2
Arc Plasma Apparatus	9.2
Glow Discharge Apparatus	9.3

Note 18212;The term “corona treatment” has been applied sometimes in the literature to the different electrical discharge treatment technologies described in Section 9. This practice defines each electrical discharge treatment technology at atmospheric pressure presented in Section 9 and draws the necessary distinctions between them and corona discharge. See Test Method D1868 for “corona discharge.”

1.4 The values stated in SI units are to be regarded as the standard.

1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. Specific hazard statements appear in Section 6.

ASTM D6105-04(2012) Referenced Document

• ASTM D1868 Standard Test Method for Detection and Measurement of Partial Discharge (Corona) Pulses in Evaluation of Insulation Systems
• ASTM D2578 Standard Test Method for Wetting Tension of Polyethylene and Polypropylene Films
• ASTM D2651 Standard Guide for Preparation of Metal Surfaces for Adhesive Bonding
• ASTM D5946 Standard Test Method for Corona-Treated Polymer Films Using Water Contact Angle Measurements
• ASTM D724 Standard Test Method for Surface Wettability of Paper (Angle-of-Contact Method)
• ASTM D907 Standard Terminology of Adhesives

ASTM D6105-04(2012) history

• 2019 ASTM D6105-04(2019) Standard Practice for Application of Electrical Discharge Surface Treatment (Activation) of Plastics for Adhesive Bonding
• 2004 ASTM D6105-04(2012) Standard Practice for Application of Electrical Discharge Surface Treatment (Activation) of Plastics for Adhesive Bonding
• 2004 ASTM D6105-04 Standard Practice for Application of Electrical Discharge Surface Treatment (Activation) of Plastics for Adhesive Bonding
• 1997 ASTM D6105-97 Standard Practice for Application of Electrical Discharge Surface Treatment (Activation) of Plastics for Adhesive Bonding