1.1 This specification covers rolled or cold-finished bar, rod, and wire in alloys (Note 1) and tempers as shown in Table 2.
Note 18212;Throughout this specification use of the term alloy in the general sense includes aluminum as well as aluminum alloy.
Note 28212;The term cold finished is used to indicate the type of surface finish, sharpness of angles, and dimensional tolerances produced by drawing through a die.
Note 38212;See Specification B221 for aluminum and aluminum-alloy extruded bars, rods, wire, shapes, and tubes; and Specification B316/B316M for aluminum and aluminum-alloy rivet and cold-heading wire and rods.
1.2 Alloy and temper designations are in accordance with ANSI H35.1. The equivalent UNS alloy designations are those of Table 1 preceded by A9, for example, A91100 for aluminum 1100 in accordance with Practice E527.
1.3 A complete metric companion to Specification B211 has been developed
1.4 For acceptance criteria for inclusion of new aluminum and aluminum alloys in this specification, see Annex A2.
TABLE 1 Chemical Composition LimitsA,B,C,D
Alloy | Si | Fe | Cu | Mn | Mg | Cr | Ni | Zn | Ti | Bi | Pb | Sn | Other ElementsE | Aluminum | |
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
Each | TotalF | ||||||||||||||
1100 | 0.95 Si + Fe | 0.05–0.20 | 0.05 | ... | ... | ... | 0.10 | ... | ... | ... | ... | 0.05 | 0.15 | 99.00 minG | |