ASTM E995-11
Standard Guide for Background Subtraction Techniques in Auger Electron Spectroscopy and X-Ray Photoelectron Spectroscopy
- Standard No.
- ASTM E995-11
- Release Date
- 2011
- Published By
- American Society for Testing and Materials (ASTM)
- Status
- Replace By
- ASTM E995-16
- Latest
- ASTM E995-16
- Scope
Background subtraction techniques in AES were originally employed as a method of enhancement of the relatively weak Auger signals to distinguish them from the slowly varying background of secondary and backscattered electrons. Interest in obtaining useful information from the Auger peak line shape, concern for greater quantitative accuracy from Auger spectra, and improvements in data gathering techniques, have led to the development of various background subtraction techniques.
Similarly, the use of background subtraction techniques in XPS has evolved mainly from the interest in the determination of chemical states (from the binding-energy values for component peaks that may often overlap), greater quantitative accuracy from the XPS spectra, and improvements in data acquisition. Post-acquisition background subtraction is normally applied to XPS data.
The procedures outlined in Section 7 are popular in XPS and AES; less popular procedures and rarely used procedures are described in Sections 8 and 9, respectively. General reviews of background subtraction methods and curve-fitting techniques have been published (1-5).
Background subtraction is usually done before peak fitting. Some commercial systems require background removal. Nevertheless, a measured spectral region consisting of one or more peaks and background intensities due to inelastic scattering, Bremsstrahlung (for XPS with unmonochromated X-ray sources), and scattered primary electrons (for AES) can often be satisfactorily represented by choosing functions for each intensity component with parameters for each component determined in a single least-squares fit. The choice of the background to be removed if required or desired before peak fitting is suggested by the experience of the analysts and the peak complexity as noted above.
1.1 The purpose of this guide is to familiarize the analyst with the principal background subtraction techniques presently in use together with the nature of their application to data acquisition and manipulation.
1.2 This guide is intended to apply to background subtraction in electron, X-ray, and ion-excited Auger electron spectroscopy (AES), and X-ray photoelectron spectroscopy (XPS).
1.3 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.
ASTM E995-11 Referenced Document
- ASTM E673 Standard Terminology Relating to Surface Analysis
ASTM E995-11 history
- 2016 ASTM E995-16 Standard Guide for Background Subtraction Techniques in Auger Electron Spectroscopy and X-Ray Photoelectron Spectroscopy
- 2011 ASTM E995-11 Standard Guide for Background Subtraction Techniques in Auger Electron Spectroscopy and X-Ray Photoelectron Spectroscopy
- 2004 ASTM E995-04 Standard Guide for Background Subtraction Techniques in Auger Electron Spectroscopy and X-ray Photoelectron Spectroscopy
- 1997 ASTM E995-97 Standard Guide for Background Subtraction Techniques in Auger Electron and X-ray Photoelectron Spectroscopy