This standard specifies micro hardness tests on
transverse sections of welded joints of metallic
materials with high hardness gradients. It covers
Vickers hardness tests in accordance with ISO DIS
6507-1, normally with test loads of 0,98 N to less than
49 N (HV 0,1 to less than HV 5).
Testing should be carried out to ensure that the highest
and/or the lowest level of hardness of both parent
metal (in the case of dissimilar parent metals) and
weld metal are determined.
The type and extent of testing shall be as specified by
an application standard or by agreement between the
contracting parties.
This standard does not cover the hardness test as
described in EN 1043-1.
BS EN ISO 9015-2:2011 history
2016BS EN ISO 9015-2:2016 Destructive tests on welds in metallic materials. Hardness testing. Microhardness testing of welded joints
2011BS EN ISO 9015-2:2011 Destructive tests on welds in metallic materials. Hardness testing. Microhardness testing of welded joints
1997BS EN 1043-2:1997 Destructive tests on welds in metallic materials - Hardness testing - Micro hardness testing on welded joints