This European Standard specifies the chemical composition limits for aluminium casting alloys and mechanical properties of separately cast test pieces for these alloys. Annex B is included as a guide to the selection of alloys for a specific use or process.This European Standard is intended to be used in conjunction with EN 576; EN 1559-1; EN 1559-4; EN 1676 and EN ISO 8062-3.
EN 1706:2010 Referenced Document
EN 10002-1 Metallic Materials - Tensile Testing - Part 1: Method of Test at Ambient Temperature
EN 12258-1:1998 Aluminium and Aluminium Alloys - Terms and Definitions - Part 1: General Terms
EN 1559-1 Founding - Technical conditions of delivery - Part 1: General*, 2011-02-01 Update
EN 1559-4 Founding - Technical conditions of delivery - Part 4: Additional requirements for aluminium alloy castings*, 2015-02-01 Update
EN 1780-1 Aluminium and aluminium alloys - Designation of alloyed aluminium ingots for remelting, master alloys and castings - Part 1: Numerical designation system*, 2024-04-19 Update
EN 1780-2 Aluminium and aluminium alloys - Designation of alloyed aluminium ingots for remelting, master alloys and castings - Part 2: Chemical symbol based designation system*, 2024-04-19 Update
EN 1780-3 Aluminium and aluminium alloys - Designation of alloyed aluminium ingots for remelting, master alloys and castings - Part 3: Writing rules for chemical compositon*, 2024-04-19 Update
EN 576 Aluminium and aluminium alloys - Unalloyed aluminium ingots for remelting - Specifications*, 2024-04-19 Update
EN ISO 6506-1 Metallic materials - Brinell hardness test - Part 1: Test method*, 2014-09-01 Update
EN 1706:2010 history
2021EN 1706:2020+A1:2021 Aluminium and aluminium alloys - Castings - Chemical composition and mechanical properties
1970EN 1706:2020 Aluminium and aluminium alloys - Castings - Chemical composition and mechanical properties
2010EN 1706:2010 Aluminium and aluminium alloys - Castings - Chemical composition and mechanical properties
1998EN 1706:1998 Aluminium and Aluminium Alloys - Castings - Chemical Composition and Mechanical Properties