ASTM B816-00(2009)
Standard Specification for Coatings of Cadmium-Zinc Mechanically Deposited
- Standard No.
- ASTM B816-00(2009)
- Release Date
- 2000
- Published By
- American Society for Testing and Materials (ASTM)
- Status
- Replace By
- ASTM B816-00(2015)
- Latest
- ASTM B816-00(2021)
- Scope
Corrosion Resistance, General8212;This functional coating is used to provide corrosion resistance. The performance of this coating depends largely on its thickness and the kind of environment to which it is exposed. Published results of environmental corrosion studies have demonstrated that the coating provides corrosion resistance greater than equivalent thicknesses of zinc coatings in industrial environments and greater corrosion resistance than equivalent thicknesses of cadmium coatings in marine environments.
Galvanic Corrosion Resistance8212;The galvanic couple that results in the corrosion of steel and aluminum parts in contact with each other in corrosive environments can also be minimized by plating the steel parts with this mechanically deposited coating.
Hydrogen Embrittlement, Absence of8212;The mechanical coating process does not produce any permanent hydrogen embrittlement in products made from high-strength steels, for example, fasteners or lock washers.
1.1 General8212;This specification covers the requirements for a coating that is a mixture of cadmium and zinc deposited on metallic products by mechanical deposition. The coating is provided in four thickness classes (see Table 1) and several finish types (see Table 2).
1.2 Toxicity8212;Warning: Cadmium is toxic; therefore these coatings should not be used on articles that will contact food or beverages, or for dental and other equipment that may be inserted into the mouth. Also, the coatings should not be used on articles that will be heated to high temperatures, because cadmium will form toxic fumes. Similarly, if coated articles are welded, soldered, or otherwise heated during fabrication, adequate ventilation should be provided to exhaust toxic fumes.
1.3 Similar Documents8212;Other kinds of mechanically deposited coatings are covered by Specifications B635, B695, and B696.
1.4 The following precautionary caveat pertains only to the test method portion, Section 9, of this specification. This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.
ASTM B816-00(2009) Referenced Document
- ASTM B117 Standard Practice for Operating Salt Spray (Fog) Apparatus
- ASTM B183 Standard Practice for Preparation of Low-Carbon Steel for Electroplating
- ASTM B242 Standard Guide for Preparation of High-Carbon Steel for Electroplating
- ASTM B320 Standard Practice for Preparation of Iron Castings for Electroplating
- ASTM B322 Standard Guide for Cleaning Metals Prior to Electroplating
- ASTM B374 Standard Terminology Relating to Electroplating
- ASTM B487 Standard Test Method for Measurement of Metal and Oxide Coating Thickness by Microscopical Examination of Cross Section
- ASTM B499 Standard Test Method for Measurement of Coating Thicknesses by the Magnetic Method: Nonmagnetic Coatings on Magnetic Basis Metals
- ASTM B571 Standard Practice for Qualitative Adhesion Testing of Metallic Coatings
- ASTM B602 Standard Test Method for Attribute Sampling of Metallic and Inorganic Coatings
- ASTM B635 Standard Specification for Coatings of Cadmium-Tin Mechanically Deposited
- ASTM B695 Standard Specification for Coatings of Zinc Mechanically Deposited on Iron and Steel
- ASTM B696 Standard Specification for Coatings of Cadmium Mechanically Deposited
- ASTM B697 Standard Guide for Selection of Sampling Plans for Inspection of Electrodeposited Metallic and Inorganic Coatings
- ASTM B762 Standard Test Method of Variables Sampling of Metallic and Inorganic Coatings
- ASTM E27 Method for Spectrographic Analysis of Zinc and Zinc Alloys by the Solution-Residue Technique
- ASTM E396 Standard Test Methods for Chemical Analysis of Cadmium
- ASTM E536 Standard Test Methods for Chemical Analysis of Zinc and Zinc Alloys
- ASTM F1470 Standard Practice for Fastener Sampling for Specified Mechanical Properties and Performance Inspection
ASTM B816-00(2009) history
- 2021 ASTM B816-00(2021) Standard Specification for Coatings of Cadmium-Zinc Mechanically Deposited
- 2000 ASTM B816-00(2015) Standard Specification for Coatings of Cadmium-Zinc Mechanically Deposited
- 2000 ASTM B816-00(2009) Standard Specification for Coatings of Cadmium-Zinc Mechanically Deposited
- 2000 ASTM B816-00(2004)e1 Standard Specification for Coatings of Cadmium-Zinc Mechanically Deposited
- 2000 ASTM B816-00 Standard Specification for Coatings of Cadmium-Zinc Mechanically Deposited
- 1991 ASTM B816-91(1997) Standard Specification for Coatings of Cadmium-Zinc Mechanically Deposited
- 1991 ASTM B816-91e1 Standard Specification for Coatings of Cadmium-Zinc Mechanically Deposited