1.1 This specification covers nickel (UNS N02200)*, low carbon nickel (UNS N02201)*, and solution strengthened nickel (UNS N02211) in the form of hot-worked and cold-worked rod and bar in the conditions shown in Table 1.
1.2 The values stated in inch-pound units are to be regarded as the standard. The values given in parentheses are for information only.
TABLE 1 Mechanical Properties
| Condition and Diameter or Distance Between Parallel Surfaces, in. (mm) | Tensile Strength, min, psi (MPa) | Yield Strength (0.2 % offset), min. psi (MPa)A | Elongation in 2 in. or 50 mm or 4D, min % |
|---|---|---|---|
| Nickel (UNS N02200) | |||
| Cold-worked (as worked): | |||
| Rounds, 1 (25.4) and under | 80 000 (550) | 60 000 (415) | 10B |
| Rounds over 1 to 4 (25.4 to 101.6) incl. | 75 000 (515) | 50 000 (345) | 15 |
| Squares, hexagons, and rectangles, all sizes | 65 000 (450) | 40 000 (275) | 25B |
| Hot-worked: | |||
| All sections, all sizes | 60 000 (415) | 15 000 (105) | 35C |
| Rings and disksD | — | — | — |
| Annealed: | |||
| Rods and bars, all sizes | 55 000 (380) | 15 000 (105) | 40B |
| Rings and disksE | — | — | — |
| Forging quality | |||
| All sizes | F | ASTM B160-05e1 history