DIN EN ISO 10270:2008 Corrosion of metals and alloys - Aqueous corrosion testing of zirconium alloys for use in nuclear power reactors (ISO 10270:1995 + Cor. 1:1997); German version EN ISO 10270:2008
This International Standard specifies:
a) the determination of mass gain;
b) the surface inspection of products of zirconium
and its alloys when corrosion tested in water at
360 ℃ or in steam at or above 400 ~C;
c) that the tests in steam shall be performed at
10,3 MPa (1 500 psi).
This International Standard is applicable to wrought
products, castings, powder metallurgy products and
weld metals.
This method has been widely used in the develop-
ment of new alloys, heat treating practices and for the
evaluation of welding techniques, and should be util-
ized in its entirety to the extent specified for a product
acceptance test, rather than merely a means of as-
sessing performance in service.
DIN EN ISO 10270:2008 history
2022DIN EN ISO 10270:2022-05 Corrosion of metals and alloys - Aqueous corrosion testing of zirconium alloys for use in nuclear power reactors (ISO 10270:2022); German version EN ISO 10270:2022
2020DIN EN ISO 10270:2020 Corrosion of metals and alloys - Aqueous corrosion testing of zirconium alloys for use in nuclear power reactors (ISO/DIS 10270:2020); German and English version prEN ISO 10270:2020
2011DIN EN ISO 10270:2011 Corrosion of metals and alloys - Aqueous corrosion testing of zirconium alloys for use in nuclear power reactors (ISO 10270:1995+Cor. 1:1997); German version EN ISO 10270:2008
2008DIN EN ISO 10270:2008 Corrosion of metals and alloys - Aqueous corrosion testing of zirconium alloys for use in nuclear power reactors (ISO 10270:1995 + Cor. 1:1997); German version EN ISO 10270:2008