DIN EN ISO 11782-1:2008 Corrosion of metals and alloys - Corrosion fatigue testing - Part 1: Cycles to failure testing (ISO 11782-1:1998); German version EN ISO 11782-1:2008
1.1 This International Standard provides guidance and instruction on corrosion fatigue testing of metals and alloys
in aqueous or gaseous environments and is concerned with cycles to failure testing. Crack propagation testing is
considered in ISO 11782-2.
1,2 Corrosive or otherwise chemically active environments can promote the initiation of fatigue cracks in metals
and alloys and increase the rate of fatigue crack propagation. Corrosion fatigue processes are not limited to specific
metal/environment systems and reliable estimates of fatigue life for all combinations of loading and environment
cannot be made without data from laboratory tests.
1.3 This International Standard is not intended for application to corrosion fatigue testing of components or parts;
nevertheless many of the general principles will apply.
DIN EN ISO 11782-1:2008 Referenced Document
ISO 7539-1:1987 Corrosion of metals and alloys - Stress corrosion testing - Part 1: General guidance on testing procedures
DIN EN ISO 11782-1:2008 history
2008DIN EN ISO 11782-1:2008-08 Corrosion of metals and alloys - Corrosion fatigue testing - Part 1: Cycles to failure testing (ISO 11782-1:1998); German version EN ISO 11782-1:2008
2008DIN EN ISO 11782-1:2008 Corrosion of metals and alloys - Corrosion fatigue testing - Part 1: Cycles to failure testing (ISO 11782-1:1998); German version EN ISO 11782-1:2008