ASTM D5365-99
Standard Test Method for Long-Term Ring-Bending Strain of "Fiberglass" (Glass-Fiber-Reinforced Thermosetting-Resin) Pipe

Standard No.

ASTM D5365-99

Release Date

1999

Published By

American Society for Testing and Materials (ASTM)

Status

Be replaced

Replace By

ASTM D5365-01

Latest

ASTM D5365-23

Scope

1.1 This test method covers a procedure for determining the long-term ring-bending strain (S _b) of "fiberglass" pipe. Both glass-fiber-reinforced thermosetting-resin pipe (RTRP) and glass-fiber-reinforced polymer mortar pipe (RPMP) are "fiberglass" pipes.

1.2 The values stated in inch-pound units are to be regarded as the standard. The SI units given in parentheses are for information only.

1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. A specific warning statement is given in 9.5.

Note 18212;There is no similar or equivalent ISO standard.

ASTM D5365-99 history

• 2023 ASTM D5365-23 Standard Test Method for Long-Term Ring-Bending Strain of “Fiberglass” (Glass-Fiber-Reinforced Thermosetting-Resin) Pipe
• 2018 ASTM D5365-18 Standard Test Method for Long-Term Ring-Bending Strain of "Fiberglass" (Glass-Fiber-Reinforced Thermosetting-Resin) Pipe
• 2012 ASTM D5365-12 Standard Test Method for Long-Term Ring-Bending Strain of ldquo;Fiberglassrdquo; (Glass-Fiber-Reinforced Thermosetting-Resin) Pipe
• 2006 ASTM D5365-06 Standard Test Method for Long-Term Ring-Bending Strain of "Fiberglass" (Glass-Fiber-Reinforced Thermosetting-Resin) Pipe
• 2001 ASTM D5365-01e1 Standard Test Method for Long-Term Ring-Bending Strain of "Fiberglass" (Glass-Fiber-Reinforced Thermosetting-Resin) Pipe
• 2001 ASTM D5365-01 Standard Test Method for Long-Term Ring-Bending Strain of "Fiberglass" (Glass-Fiber-Reinforced Thermosetting-Resin) Pipe
• 1999 ASTM D5365-99 Standard Test Method for Long-Term Ring-Bending Strain of "Fiberglass" (Glass-Fiber-Reinforced Thermosetting-Resin) Pipe