SAE AMS4152M-2007
Aluminum Alloy Extrusions 4.4Cu - 1.5Mg - 0.60Mn (2024-T3) Solution Heat Treated UNS A92024

Standard No.

SAE AMS4152M-2007

Release Date

2007

Published By

Society of Automotive Engineers (SAE)

Status

Be replaced

Replace By

SAE AMS4152K-2011

Latest

SAE AMS4152N-2019

Scope

This specification covers an aluminum alloy in the form of extruded bars, rods, wire, shapes, and tubing. Primarily for parts requiring good strength and whose fabrication does not involve welding, but usage is not limited to such applications. Certain processing procedures may cause these products to be susceptible to stress-corrosion cracking; ARP 823 recommends practices to minimize such conditions.

SAE AMS4152M-2007 Referenced Document

• ASTM B594-06 Standard Practice for Ultrasonic Inspection of Aluminum-Alloy Wrought Products for Aerospace Applications*， 2024-04-18 Update
• ASTM B660-02 Standard Practices for Packaging/Packing of Aluminum and Magnesium Products*， 2024-04-18 Update
• ASTM B666/B666M-01 Standard Practice for Identification Marking of Aluminum and Magnesium Products*， 2024-04-18 Update
• SAE AMS2355H-2005 Quality Assurance Sampling and Testing of Aluminum Alloys and Magnesium Alloys, Wrought Products, Except Forging Stock, and Rolled, Forged, or Flash Welded Rings
• SAE AMS2772-1997 Heat Treatment of Aluminum Alloy Raw Materials (01 1997)
• SAE ARP823 MINIMIZING STRESS CORROSION IN WROUGHT HEAT TREATABLE ALUMINUM ALLOY PRODUCTS
• SAE ARP823D-1997 Minimizing Stress-Corrosion in Wrought Heat-Treatable Aluminum Alloy Products
• SAE AS1990-1990 Aluminum Alloy Tempers

SAE AMS4152M-2007 history

• 2019 SAE AMS4152N-2019 Aluminum Alloy Extrusions 4.4Cu - 1.5Mg - 0.60Mn (2024-T3) Solution Heat Treated and Cold Worked
• 2018 SAE AMS4152M-2018 Aluminum Alloy Extrusions 4.4Cu - 1.5Mg - 0.60Mn (2024-T3) Solution Heat Treated
• 2011 SAE AMS4152K-2011 ALUMINUM ALLOY EXTRUSIONS 4.4Cu - 1.5Mg - 0.60Mn (2024-T3) Solution Heat Treated
• 2007 SAE AMS4152M-2007 Aluminum Alloy Extrusions 4.4Cu - 1.5Mg - 0.60Mn (2024-T3) Solution Heat Treated UNS A92024
• 2000 SAE AMS4152L-2000 Aluminum Alloy Extrusions 4.4Cu - 1.5Mg - 0.60Mn (2024-T3) Solution Heat Treated
• 1993 SAE AMS4152L-1993 Aluminum Alloy, Extrusions 4.4Cu 1.5Mg 0.60Mn Solution Heat Treated
• 1987 SAE AMS4152K-1987 Aluminum Alloy Extrusions 4.4Cu - 1.5Mg - 0.60Mn (2024-T3) Solution Heat Treated (UNS A92024)
• 1978 SAE AMS4152J-1978 ALUMINUM ALLOY EXTRUSIONS 4.4Cu - 1.5Mg - 0.60Mn (2024-T3)
• 1967 SAE AMS4152H-1967 ALUMINUM ALLOY EXTRUSIONS 4.4Cu - 1.5Mg - 0.60Mn (2024-T4)
• 1964 SAE AMS4152G-1964 ALUMINUM ALLOY EXTRUSIONS 4.5Cu - 1.5Mg - 0.60Mn (2024-T4)
• 1956 SAE AMS4152F-1956 ALUMINUM ALLOY EXTRUSIONS 4.5Cu - 1.5Mg - 0.6Mn (2024-T4)
• 1952 SAE AMS4152E-1952 ALUMINUM ALLCY EXTRUSIONS 4.3Cu - 1.5Mg - 0.6Mn (24S-T4)
• 1946 SAE AMS4152D-1946 ALUMINUM ALLOY BARS (EXTRUDED) Copper Magnesium Manganese (24S-T)
• 1946 SAE AMS4152C-1946 ALUMINUM ALLOY BARS (EXTRUDED) Copper Magnesium Manganese (24S-T)
• 1943 SAE AMS4152B-1943 ALUMINUM ALLOY Copper Magnesium Manganese (24S-T) Extruded
• 1942 SAE AMS4152A-1942 ALUMINUM ALLOY EXTRUSIONS Copper Magnesium Manganese (24S-T)
• 1941 SAE AMS4152-1941 ALUMINUM ALLOY EXTRUSIONS Heat Treated Copper Magnesium Manganese (24S-T)