SAE AMS3711E-2001
Core, Honeycomb Fibrous, Aramid Base, Phenolic Coated

Standard No.

SAE AMS3711E-2001

Release Date

2001

Published By

Society of Automotive Engineers (SAE)

Status

Be replaced

Replace By

SAE AMS3711E-2013

Latest

SAE AMS3711E-2013

Scope

This specification covers expanded honeycomb core made of fibrous aramid paper sheets and supplied in the form of blocks, slices, and ordered shapes. This honeycomb core has been used typically for bonded sandwich structures requiring high strength and corrosion resistance in the temperature range -65 to +180 °F (-54 to +82 °C), but usage is not limited to such applications.

SAE AMS3711E-2001 Referenced Document

• ASTM C271-99 Standard Test Method for Density of Sandwich Core Materials
• ASTM C363-00 Standard Test Method for Delamination Strength of Honeycomb Core Materials*， 2024-04-18 Update
• ASTM C365-00 Standard Test Method for Flatwise Compressive Properties of Sandwich Cores*， 2024-04-18 Update
• ASTM F501-93 

SAE AMS3711E-2001 history

• 2013 SAE AMS3711E-2013 Core, Honeycomb Fibrous, Aramid Base, Phenolic Coated
• 2001 SAE AMS3711E-2001 Core, Honeycomb Fibrous, Aramid Base, Phenolic Coated
• 1999 SAE AMS3711D-1999 CORE, HONEYCOMB Fibrous, Aramid Base, Phenolic Coated
• 1993 SAE AMS3711D-1993 Core@ Honeycomb Fibrous@ Aramid Base@ Phenolic Coated
• 1988 SAE AMS3711C-1988 CORE, HONEYCOMB, FIBROUS ARAMID BASE, PHENOLIC COATED
• 1979 SAE AMS3711B-1979 CORE, HONEYCOMB, FIBROUS ARAMID BASE, PHENOLIC COATED
• 1976 SAE AMS3711A-1976 CORE, HONEYCOMB, FIBROUS ARAMID BASE, PHENOLIC COATED
• 1974 SAE AMS3711-1974 CORE, HONEYCOMB, FIBROUS NYLON BASE, PHENOLIC COATED