SAE AMS4153K-2003
Aluminum Alloy, Extrusions 4.5Cu 0.85Si 0.80Mn 0.50Mg (2014-T6) Solution and Precipitation Heat Treated

Standard No.

SAE AMS4153K-2003

Release Date

2003

Published By

Society of Automotive Engineers (SAE)

Status

Be replaced

Replace By

SAE AMS4153K-2008

Latest

SAE AMS4153M-2020

Scope

This specification covers an aluminum alloy in the form of extruded bars, rods, wire, shapes and tubing. These products have been used typically for parts requiring good strength and where fabrication does not usually involve welding, but usage is not limited to such applications. Certain design and processing procedures may cause these extrusions to be susceptible to stress-corrosion cracking; SAE ARP 823 recommends practices to minimize such conditions.

SAE AMS4153K-2003 Referenced Document

• ASTM B594-02 Standard Practice for Ultrasonic Inspection of Aluminum-Alloy Wrought Products for Aerospace Applications*， 2024-04-18 Update
• ASTM B660-02 Standard Practices for Packaging/Packing of Aluminum and Magnesium Products*， 2024-04-18 Update
• ASTM B666/B666M-01 Standard Practice for Identification Marking of Aluminum and Magnesium Products*， 2024-04-18 Update
• SAE AMS2355G-2002 Quality Assurance, Sampling and Testing Aluminum Alloys and Magnesium Alloys Wrought Products, Except Forging Stock, and Rolled, Forged, or Flash Welded Rings
• SAE AMS2772-1997 Heat Treatment of Aluminum Alloy Raw Materials (01 1997)
• SAE ARP823 MINIMIZING STRESS CORROSION IN WROUGHT HEAT TREATABLE ALUMINUM ALLOY PRODUCTS
• SAE ARP823D-1997 Minimizing Stress-Corrosion in Wrought Heat-Treatable Aluminum Alloy Products
• SAE AS1990-1990 Aluminum Alloy Tempers

SAE AMS4153K-2003 history

• 2020 SAE AMS4153M-2020 Aluminum Alloy, Extrusions 4.5Cu - 0.85Si - 0.80Mn - 0.50Mg (2014-T6) Solution and Precipitation Heat Treated
• 2015 SAE AMS4153L-2015 Aluminum Alloy@ Extrusions 4.5Cu - 0.85Si - 0.80Mn - 0.50Mg (2014-T6) Solution and Precipitation Heat Treated (UNS A92014)
• 2008 SAE AMS4153K-2008 Aluminum Alloy, Extrusions 4.5Cu - 0.85Si - 0.80Mn - 0.50Mg (2014-T6) Solution and Precipitation Heat Treated
• 2003 SAE AMS4153K-2003 Aluminum Alloy, Extrusions 4.5Cu 0.85Si 0.80Mn 0.50Mg (2014-T6) Solution and Precipitation Heat Treated
• 1998 SAE AMS4153J-1998 Aluminum Alloy Extrusions 4.5Cu - 0.85Si - 0.80Mn - 0.50Mg (2014 -T6) Solution and Precipitation Heat Treated (UNS A92014)
• 1990 SAE AMS4153H-1990 Aluminum Alloy Extrusions 4.5Cu - 0.85Si - 0.80Mn - 0.50Mg (2014 -T6) Solution and Precipitation Heat Treated
• 1978 SAE AMS4153G-1978 ALUMINUM ALLOY EXTRUSIONS 4.5Cu - 0.85Si - 0.80Mn - 0.50Mg (2014-T6)
• 1968 SAE AMS4153F-1968 ALUMINUM ALLOY EXTRUSIONS 4.5Cu - 0.85Si - 0.80Mn - 0.50Mg (2014-T6)
• 1967 SAE AMS4153E-1967 ALUMINUM ALLOY EXTRUSIONS 4.5Cu - 0.85Si - 0.80Mn - 0.50Mg (2014-T6)
• 1967 SAE AMS4153D-1967 ALUMINUM ALLOY EXTRUSIONS 4.5Cu - 0.85Si - 0.80Mn - 0.50Mg (2014-T6)
• 1966 SAE AMS4153C-1966 ALUMINUM ALLOY EXTRUSIONS 4.5Cu - 0.85Si - 0.80Mn - 0.50Mg (2014-T6)
• 1962 SAE AMS4153B-1962 ALUMINUM ALLOY EXTRUSIONS 4.5Cu - 0.9Si - 0.8Mn - 0.5Mg (2014-T6)
• 1952 SAE AMS4153A-1952 ALUMINUM ALLOY EXTRUSIONS 4.5Cu - 0.9Si - 0.8Mn - 0.5Mg (14S-T6)
• 1946 SAE AMS4153-1946 ALUMINUM ALLOY BARS (EXTRUDED) Copper Silicon Manganese Magnesium (14S-T)