SAE AMS5355H-2001
Steel, Corrosion Resistant, Investment Castings 16Cr 4.1Ni 0.28Cb 3.2Cu Homogenization and Solution Heat Treated or Homogenization, Solution, and Precipitation Heat Treated

Standard No.

SAE AMS5355H-2001

Release Date

2001

Published By

Society of Automotive Engineers (SAE)

Status

Withdraw

Replace By

SAE AMS5355H-2006

Latest

SAE AMS5355J-2022

Scope

This specification covers a corrosion-resistant steel in the form of investment castings. These castings have been used typically for parts requiring good corrosion resistance and strength up to 600 degrees F (316 degrees C), but usage is not limited to such applications. Certain processing procedures and service conditions may cause these castings to become subject to stress-corrosion cracking; ARP1110 recommends practices to minimize such conditions. Where stress-corrosion is considered to be a factor, precipitation heat treatment should be performed at a temperature not lower than 1000 degrees F (538 degrees C).

SAE AMS5355H-2001 history

• 2022 SAE AMS5355J-2022 Steel, Corrosion-Resistant, Investment Castings 16Cr - 4.1Ni - 0.28Cb - 3.2Cu Homogenization and Solution Heat Treated or Homogenization, Solution, and Precipitation Heat Treated
• 2011 SAE AMS5355D-2011 STEEL CASTINGS, INVESTMENT, CORROSION RESISTANT 16Cr - 4.1Ni - 0.28 (Cb+Ta) - 3.2Cu Solution Heat Treated
• 2009 SAE AMS5355J-2009 Steel, Corrosion Resistant, Investment Castings 16Cr 4.1Ni 0.28Cb 3.2Cu Homogenization and Solution Heat Treated or Homogenization, Solution, and Precipitation Heat Treated
• 2006 SAE AMS5355H-2006 Steel, Corrosion Resistant, Investment Castings 16Cr - 4.1Ni - 0.28Cb - 3.2Cu Homogenization and Solution Heat Treated or Homogenization, Solution, and Precipitation Heat Treated
• 2001 SAE AMS5355H-2001 Steel, Corrosion Resistant, Investment Castings 16Cr 4.1Ni 0.28Cb 3.2Cu Homogenization and Solution Heat Treated or Homogenization, Solution, and Precipitation Heat Treated
• 2001 SAE AMS5355G-2001 Steel@ Corrosion Resistant@ Investment Castings 16Cr - 4.1Ni - 0.28Cb - 3.2Cu Homogenization and Solution Heat Treated or Homogenization@ Solution@ and Precipitation Heat Treated (UNS J92200)
• 1995 SAE AMS5355F-1995 Steel Castings@ Investment@ Corrosion Resistant 16Cr - 4.1Ni - 3.15Cu
• 1994 SAE AMS5355E-1994 Steel Castings@ Investment@ Corrosion Resistant 16Cr - 4.1Ni - 3.15Cu
• 1985 SAE AMS5355D-1985 Steel Castings@ Investment@ Corrosion Resistant 16Cr - 4.1Ni - 0.28 (Cb+Ta) - 3.2Cu Solution Heat Treated (UNS J92200)
• 1977 SAE AMS5355C-1977 Steel Castings@ Investment@ Corrosion Resistant 16Cr - 4.1Ni - 0.28(Cb+Ta) 3.2Cu
• 1969 SAE AMS5355B-1969 Steel Castings@ Investment@ Corrosion Resistant 16Cr - 4.1Ni - 3.15Cu
• 1960 SAE AMS5355A-1960 Steel Castings@ Investment@ Corrosion Resistant 16Cr - 4.1Ni - 3.15Cu
• 1955 SAE AMS5355-1955 Steel Castings@ Precision Investment@ Corrosion Resistant 17Cr - 4Ni - 4Cu
• 1944 SAE AMS5355E-1944 STEEL, CORROSION RESISTANT, INVESTMENT CASTINGS 16Cr - 4.1Ni - 0.28Cb - 3.2Cu Homogenization and Solution Heat Treated or Homogenization, Solution, and Precipitation Heat Treated