SAE AMS4766G-1999
Silver Alloy, Brazing Filler Metal 85Ag - 15Mn 1760 Degrees to 1780 Degrees F (960 Degrees to 971 Degrees C) Solidus-Liquidus Range UNS P07850

Standard No.

SAE AMS4766G-1999

Release Date

1999

Published By

Society of Automotive Engineers (SAE)

Status

Withdraw

Replace By

SAE AMS4766G-2009

Latest

SAE AMS4766J-2021

Scope

This specification covers a silver alloy in the form of wire, rod, sheet, strip, foil, pig, powder, shot, and chips and a viscous mixture (paste) of powder in a suitable binder. This material has been used typically for joining ferrous metals where high strength up to 800 degrees F (427 degrees C) for short-time service or up to 500 degrees F (260 degrees C) for long-time service is required, and for joining nonferrous metals except those having a base of aluminum or magnesium, but usage is not limited to such applications.

SAE AMS4766G-1999 Referenced Document

• ASTM B214-99 Standard Test Method for Sieve Analysis of Metal Powders*， 1999-04-10 Update
• SAE AMS2222 TOLERANCES Copper and Copper Alloy Plate@ Sheet and Strip
• SAE AMS2222H-1994 Tolerances, Copper and Copper Alloy Sheet, Strip, and Plate
• SAE AMS2224 Tolerances Copper and Copper Alloy Wire
• SAE AMS2224F-1993 Tolerances, Copper and Copper Alloy Wire
• SAE MAM2222 Tolerances@ Metric Copper and Copper Alloy Sheet@ Strip@ and Plate
• SAE MAM2224 TOLERANCES, METRIC Copper and Copper Alloy Wire

SAE AMS4766G-1999 history

• 2021 SAE AMS4766J-2021 Silver Alloy, Brazing Filler Metal 85Ag - 15Mn 1760 to 1780 °F (960 to 971 °C) Solidus-Liquidus Range (UNS P07850)
• 2015 SAE AMS4766H-2015 Silver Alloy@ Brazing Filler Metal 85Ag - 15Mn 1760 to 1780 ��(960 to 971 �� Solidus-Liquidus Range (UNS P07850)
• 2009 SAE AMS4766G-2009 Silver Alloy, Brazing Filler Metal 85Ag - 15Mn 1760 to 1780 °F (960 to 971 °C) Solidus-Liquidus Range
• 1999 SAE AMS4766G-1999 Silver Alloy, Brazing Filler Metal 85Ag - 15Mn 1760 Degrees to 1780 Degrees F (960 Degrees to 971 Degrees C) Solidus-Liquidus Range UNS P07850
• 1992 SAE AMS4766F-1992 Silver Alloy Brazing Filler Metal 85Ag - 15Mn 1760 Degrees to 1780 Degrees F (960 Degrees to 971 Degrees C) Solidus-Liquidus Range
• 1991 SAE AMS4766E-1991 BRAZING FILLER METAL@ SILVER 85Ag - 15Mn 1760° - 1780°F (960° to 970°C) Solidus-Liquidus Range (UNS P07850)
• 1984 SAE AMS4766D-1984 BRAZING FILLER METAL@ SILVER 85Ag - 15Mn 1760° - 1780°F (960° to 970°C) Solidus-Liquidus Range (UNS P07850)
• 1978 SAE AMS4766C-1978 BRAZING FILLER METAL@ SILVER 85Ag - 15Mn 1760° - 1780°F (960° to 970°C) Solidus-Liquidus Range (UNS P07850)
• 1966 SAE AMS4766B-1966 BRAZING ALLOY@ SILVER 85Ag - 15Mn
• 1960 SAE AMS4766A-1960 BRAZING ALLOY@ SILVER 85Ag - 15Mn
• 1954 SAE AMS4766-1954 BRAZING ALLOY@ SILVER 85Ag - 15Mn