SAE AMS6325G-1994
Steel Bars and Forgings, 0.50Cr 0.55Ni 0.25Mo (0.38-0.43C) Heat Treated, 105 ksi (724 MPa) Tensile Strength (Reaffirmed: 01 Sept 2000)

Standard No.

SAE AMS6325G-1994

Release Date

1994

Published By

Society of Automotive Engineers (SAE)

Status

Withdraw

Replace By

SAE AMS6325G-2000

Latest

SAE AMS6325L-2020

Scope

This specification covers an aircraft-quality, low-alloy steel in the form of heat treated bars and forgings. These products have been used typically for parts, such as nuts, bolts, and screws, 1.750 inches (44.45 mm) and under in section thickness requiring a minimum tensile strength of 105 ksi (724 MPa), but usage is not limited to such applications.

SAE AMS6325G-1994 history

• 2020 SAE AMS6325L-2020 Steel, Bars, and Forgings 0.50Cr - 0.55Ni - 0.25Mo (0.38 - 0.43C) (SAE 8740) Heat Treated, 105 ksi (724 MPa) Tensile Strength
• 2015 SAE AMS6325K-2015 Steel@ Bars@ and Forgings 0.50Cr - 0.55Ni - 0.25Mo (0.38 - 0.43C) (SAE 8740) Heat Treated@ 105 ksi (724 MPa) Tensile Strength (UNS G87400)
• 2010 SAE AMS6325J-2010 Steel Bars and Forgings, 0.50Cr 0.55Ni 0.25Mo (0.38-0.43C) (SAE 8740) Heat Treated, 105 ksi (724 MPa) Tensile Strength
• 2004 SAE AMS6325H-2004 Steel Bars and Forgings, 0.50Cr 0.55Ni 0.25Mo (0.38-0.43C) (SAE 8740) Heat Treated, 105 ksi (724 MPa) Tensile Strength
• 2000 SAE AMS6325G-2000 Steel, Bars and Forgings 0.50Cr - 0.55Ni - 0.25Mo (0.38 - 0.43C) (SAE 8740) Heat Treated, 105 ksi (724 MPa) Tensile Strength
• 1994 SAE AMS6325G-1994 Steel Bars and Forgings, 0.50Cr 0.55Ni 0.25Mo (0.38-0.43C) Heat Treated, 105 ksi (724 MPa) Tensile Strength (Reaffirmed: 01 Sept 2000)
• 1988 SAE AMS6325F-1988 STEEL BARS AND FORGINGS 0.50Cr - 0.55Ni - 0.25Mo (0.38 - 0.43C) (SAE 8740) Heat Treated@ 105@ 000 psi (724 MPa) Tensile Strength (UNS G87400)
• 1972 SAE AMS6325E-1972 STEEL BARS AND FORGINGS 0.50Cr - 0.55Ni - 0.25Mo (0.38 - 0.43C) (SAE 8740) Heat Treated@ 105@ 000 psi (724 MPa) Tensile Strength
• 1966 SAE AMS6325D-1966 STEEL BARS AND FORGINGS 0.50Cr - 0.55Ni - 0.25Mo (0.38 - 0.43C) (SAE 8740) Heat Treated (105@ 000 psi Tensile)
• 1951 SAE AMS6325C-1951 STEEL 0.55Ni - 0.5Cr - 0.25Mo (0.38 - 0.43C) (SAE 8740) Heat Treated (105000TS)
• 1945 SAE AMS6325B-1945 STEEL .55 Ni .5 Cr .25 Mo (.38 - .43 C) Heat Treated (105@000 TS)
• 1943 SAE AMS6325A-1943 STEEL .55 Ni .5 Cr .25 Mo (.38-.43 C) (105@000 TS)
• 1942 SAE AMS6325-1942 STEEL .5 Ni .5 Cr .25 Mo (.38-.43 C) (105@000 TS)