APPLICATION: Primarily for joining ferrous metals@ including austenitic stainless steels@ where moderate joint strength up to 600 F (316 C) for short time service or 400 F (204 C) for long time service is required@ or for nonferrous alloys except those having base of aluminum or magnesium. This alloy is particularly suitable for brazing in brazing in hydrogen or inert atmosphere.
SAE AMS4773A-1966 history
2021SAE AMS4773H-2021 Silver Alloy, Brazing Filler Metal 60Ag - 30Cu - 10Sn 1115 to 1325 °F (602 to 718 °C) Solidus-Liquidus Range (UNS P07600)
2016SAE AMS4773G-2016 Silver Alloy@ Brazing Filler Metal 60Ag – 30Cu – 10Sn 1115 to 1325 °F (602 to 718 °C) Solidus-Liquidus Range (UNS P07600)
2009SAE AMS4773F-2009 Silver Alloy, Brazing Filler Metal 60Ag - 30Cu - 10Sn 1115 to 1325 °F (602 to 718 °C) Solidus-Liquidus Range
1999SAE AMS4773F-1999 Silver Alloy, Brazing Filler Metal 60Ag 30Cu 10Sn 1115 to 1325 °F (602 to 718°C) Solidus-Liquidus Range