ASTM D8377-21a PDF

Scope: 1.1 This guide covers the best practice for strength measurements at elevated temperature of graphite impregnated with molten salt. 1.2 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard. 1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. 1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ASTM D8377-21a Referenced Document

ASTM C651 Standard Test Method for Flexural Strength of Manufactured Carbon and Graphite Articles Using Four-Point Loading at Room Temperature
ASTM C695 Standard Test Method for Compressive Strength of Carbon and Graphite
ASTM C749 Standard Test Method for Tensile Stress-Strain of Carbon and Graphite
ASTM D4175 Standard Terminology Relating to Petroleum Products, Liquid Fuels, and Lubricants*， 2023-07-01 Update
ASTM D8091 Standard Guide for Impregnation of Graphite with Molten Salt*， 2024-04-22 Update
ASTM D8289 Standard Test Method for Tensile Strength Estimate by Disc Compression of Manufactured Graphite
ASTM E4 Standard Practices for Force Verification of Testing Machines

2021 ASTM D8377-21a Standard Guide for High Temperature Strength Measurements of Graphite Impregnated with Molten Salt
2021 ASTM D8377-21 Standard Guide for High Temperature Strength Measurements of Graphite Impregnated with Molten Salt